Low-temperature graphitization of amorphous carbon nanospheres

doi:10.1016/S1872-2067(14)60098-X

催化学报 ›› 2014, Vol. 35 ›› Issue (6): 869-876.DOI: 10.1016/S1872-2067(14)60098-X

Low-temperature graphitization of amorphous carbon nanospheres

Katia Barbera^a, Leone Frusteri^a, Giuseppe Italiano^b, Lorenzo Spadaro^c, Francesco Frusteri^c, Siglinda Perathoner^a, Gabriele Centi^a

a University of Messina and INSTM/CASPE (Lab. of Catalysis for Sustainable Production and Energy), Department of Electronic Engineering, Industrial Chemistry and Engineering-Contrada di Dio I-98166 Messina, Italy;
b Eco-Rigen S. r. l. R&D-Contrada Piana del Signore c/o Raffineria di Gela, I-93012 Gela (CL), Italy;
c Institute of Advanced Technologies for Energy "Nicola Giordano" (ITAE), Department of Energy and Transport (DET), National Council of Research (CNR)-Salita S. Lucia sopra Contesse 5 I-98126, Messina, Italy

收稿日期:2014-03-20 修回日期:2014-04-09 出版日期:2014-05-30 发布日期:2014-06-03
通讯作者: Katia Barbera
基金资助:
This work was supported by EU project INCAS "Integration of Nanoreactor and multisite CAtalysis for a Sustainable chemical production" (Grant agreement no: 245988), in the frame of which part of this work was realized.

Low-temperature graphitization of amorphous carbon nanospheres

Katia Barbera^a, Leone Frusteri^a, Giuseppe Italiano^b, Lorenzo Spadaro^c, Francesco Frusteri^c, Siglinda Perathoner^a, Gabriele Centi^a

a University of Messina and INSTM/CASPE (Lab. of Catalysis for Sustainable Production and Energy), Department of Electronic Engineering, Industrial Chemistry and Engineering-Contrada di Dio I-98166 Messina, Italy;
b Eco-Rigen S. r. l. R&D-Contrada Piana del Signore c/o Raffineria di Gela, I-93012 Gela (CL), Italy;
c Institute of Advanced Technologies for Energy "Nicola Giordano" (ITAE), Department of Energy and Transport (DET), National Council of Research (CNR)-Salita S. Lucia sopra Contesse 5 I-98126, Messina, Italy

Received:2014-03-20 Revised:2014-04-09 Online:2014-05-30 Published:2014-06-03
Supported by:
This work was supported by EU project INCAS "Integration of Nanoreactor and multisite CAtalysis for a Sustainable chemical production" (Grant agreement no: 245988), in the frame of which part of this work was realized.

摘要/Abstract

摘要：

The investigation by SEM/TEM, porosity, and X-ray diffraction measurements of the graphitization process starting from amorphous carbon nanospheres, prepared by glucose carbonization, is reported. Aspects studied are the annealing temperature in the 750-1000℃ range, the type of inert carrier gas, and time of treatment in the 2-6 h range. It is investigated how these parameters influence the structural and morphological characteristics of the carbon materials obtained as well as their nanostructure. It is shown that it is possible to maintain after graphitization the round-shaped macro morphology, a high surface area and porosity, and especially a large structural disorder in the graphitic layers stacking, with the presence of rather small ordered domains. These are characteristics interesting for various catalytic applications. The key in obtaining these characteristics is the thermal treatment in a flow of N₂. It was demonstrated that the use of He rather than N₂ does not allow obtaining the same results. The effect is attributed to the presence of traces of oxygen, enough to create the presence of oxygen functional groups on the surface temperatures higher than 750℃, when graphitization occurs. These oxygen functional groups favor the graphitization process.

关键词: Graphitization, Carbon nanospheres, Carbon structural disorder

Abstract:

Key words: Graphitization, Carbon nanospheres, Carbon structural disorder

Katia Barbera, Leone Frusteri, Giuseppe Italiano, Lorenzo Spadaro, Francesco Frusteri, Siglinda Perathoner, Gabriele Centi. Low-temperature graphitization of amorphous carbon nanospheres[J]. 催化学报, 2014, 35(6): 869-876.

×
扫码分享

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://www.cjcatal.com/CN/10.1016/S1872-2067(14)60098-X

https://www.cjcatal.com/CN/Y2014/V35/I6/869

参考文献

[1] Su D S, Perathoner S, Centi G. Chem Rev, 2013, 113: 5782
[2] Mleczko L, Lolli G. Angew Chem Int Ed, 2013, 52: 9372
[3] Vilatela J J, Eder D. ChemSusChem, 2012, 5: 456
[4] Su C, Loh K P. Acc Chem Res, 2013, 46: 2275
[5] Dreyer D R, Bielawski C W. Chem Sci, 2011, 2: 1233
[6] Dreyer D R, Jia H P, Bielawski C W. Angew Chem Int Ed, 2010, 49: 6813
[7] Schaetz A, Zeltner M, Stark W J. ACS Catal, 2012, 2: 1267
[8] Su C, Acik M, Takai K, Lu J, Hao S J, Zheng Y, Wu P P, Bao Q L, Enoki T, Chabal Y J, Loh K P. Nat Commun, 2012, 3:1298
[9] Centi G, Perathoner S. Catal Today, 2010, 150: 151
[10] Centi G, Perathoner S. ChemSusChem, 2011, 4: 913
[11] Bitter J H. J Mater Chem, 2010, 20: 7312
[12] Su D S, Schlögl R. ChemSusChem, 2010, 3: 136
[13] Umeyama T, Imahori H. J Phys Chem C, 2013, 117: 3195
[14] Centi G, Perathoner S. Eur J Inorg Chem, 2009, 26: 3851
[15] Centi G, Perathoner S. Coord Chem Rev, 2011, 255: 1480
[16] Su D S, Zhang J, Frank B, Thomas A, Wang X C, Paraknowitsch J, Schlögl R. ChemSusChem, 2010, 3: 169
[17] Yu D S, Nagelli E, Du F, Dai L M. J Phys Chem Lett, 2010, 1: 2165
[18] Sun X Y, Wang R, Su D S. Chin J Catal (催化学报), 2013, 34: 508
[19] Yang Z, Nie H G, Chen X A, Chen X H, Huang S M. J Power Sources, 2013, 236: 238
[20] Zhang M, Dai L M. Nano Energy, 2012, 1: 514
[21] Zheng Y, Jiao Y, Jaroniec M, Jin Y G, Qiao S Z. Small, 2012, 8: 3550
[22] Powles R C, Marks N A, Lau D W M. Phys Rev B, 2009, 79: 075430
[23] Zhang J, Liu X, Blume R, Zhang A H, Schlögl R, Su D S. Science, 2008, 322: 73
[24] Liu X, Frank B, Zhang W, Cotter T P, Schlögl R, Su D S. Angew Chem Int Ed, 2011, 50: 3318
[25] Frank B, Zhang J, Blume R, Schlögl R, Su D S. Angew Chem Int Ed, 2009, 48: 6913
[26] Frank B, Blume R, Rinaldi A, Trunschke A, Schlögl R. Angew Chem Int Ed, 2011, 50: 1
[27] Cotarca L, Eckert H. Phosgenations-A Handbook. Weinheim: Wiley-VCH, 2003
[28] Mitchell C J, van der Borden W, van der Velde K, Smit M, Scheringa R, Ahrika K, Jones D H. Catal Sci Technol, 2012, 2: 2109
[29] Volodina V A, Kozlovskii A A, Kuzina S I, Mikhailov A I. High Energy Chem, 2008, 42: 311
[30] Zhang Z L, Wang Y H, Tan Q Q, Li D, Chen Y F, Zhong Z Y, Su F B. Nanoscale, 2014, 6: 371
[31] Meng Q N, Zhang F F, Wang L M, Xiang S Y, Zhu S J, Zhang G Y, Zhang K, Yang B. RSC Adv, 2014, 4: 713
[32] Chang B B, Guan D X, Tian Y L, Yang Z C, Dong X P. J Hazard Mater, 2013, 262: 256
[33] He G, Evers S, Liang X, Cuisinier M, Garsuch A, Nazar L F. ACS Nano, 2013, 7: 10920
[34] Yu X L, Wang J G, Huang Z H, Shen W C, Kang F Y. Electrochem Commun, 2013, 36: 66
[35] Xiao J P, Yao M G, Zhu K, Zhang D, Zhao S J, Lu S C, Liu B, Cui W, Liu B B. Nanoscale, 2013, 5: 11306
[36] Chang B B, Tian Y L, Shi W W, Liu J Y, Xi F N, Dong X P. RSC Adv, 2013, 3: 20999
[37] You C H, Liao S J, Li H L, Hou S Y, Peng H L, Zeng X Y, Liu F F, Zheng R P, Fu Z Y, Li Y W. Carbon, 2014, 69: 294
[38] Song X H, Wang Y B, Wang K, Xu R. Ind Eng Chem Res, 2012, 51: 13438
[39] Zhai D Y, Du H D, Li B H, Zhu Y A, Kang F Y. Carbon, 2011, 49: 725
[40] Fuertes A B, Alvarez S. Carbon, 2004, 42: 3049
[41] Asaka K, Karita M, Saito Y. Appl Phys Lett, 2011, 99: 091907
[42] Sevilla M, Sanchis C, Valdes-Solis T, Morallon E, Fuertes A B. J Phys Chem C, 2007, 111: 9749
[43] Ramos A, Caméan I, Garcìa A B. Carbon, 2013, 59: 2
[44] Briston K J, Martin J M, Heau C, Martin M, Inkson B J. Nanotechnology, 2012, 23: 485602
[45] Sevilla M, Fuertes A B. Carbon, 2006, 44: 468
[46] Kasahara N, Shiraishi S, Oya A. Carbon, 2003, 41: 1654
[47] Frusteri L, Cannilla C, Barbera K, Perathoner S, Centi G, Frusteri F. Carbon, 2013, 59: 296
[48] Nieto-Marquez A, Espartera I, Lazo J C, Romero A, Valverde J L. Chem Eng J, 2009, 153: 211
[49] Genovese C, Ampelli C, Perathoner S, Centi G. J Energy Chem, 2013, 22: 202
[50] Su D S, Centi G. J Energy Chem, 2013, 22: 151
[51] Thommes M. Chem Ing Technol, 2010, 82: 1059
[52] Jiang J X, Su F B, Trewin A, Wood C D, Campbell N L, Niu H, Dickinson C, Ganin A Y, Rosseinsky M J, Khimyak Y Z, Cooper A I. Angew Chem Int Ed, 2007, 46: 8574
[53] Antonov D, Häußermann T, Aird A, Roth J, Trebin H-R, Müller C, McGuiness L, Jelezko F, Yamamoto T, Isoya J, Pezzagna S, Meijer J, Wrachtrup J. Mater Sci, 2013, arXiv:1303.3730
[54] Norfolk C, Kaufmann A, Mukasyan A, Varma A. Carbon, 2006, 44: 301
[55] Ungar T, Gubicza J, Ribarik G, Pantea C, Zerda W. Carbon, 2002, 40: 929
[56] Biscoe J, Warren B E. J Appl Phys, 1942, 13: 364
[57] Hays D, Patrick J W, Walker A. Fuel, 1983, 62: 1079
[58] Aminzadeh A. Appl Spectroscopy, 1997, 51: 817
[59] Stair P C. Adv Catal, 2007, 51: 75
[60] Ferrari A C, Robertson J. Phys Rev B, 2000, 61: 14095
[61] Chu P K, Li L H. Mater Chem Phys, 2006, 96: 253
[62] Ferrari A C, Rodil S E, Robertson J. Phys Rev B, 2003, 67: 155306
[63] Tang Z H, Zhang L Q, Zeng C F, Lin T F, Guo B C. Soft Matter, 2012, 8: 921
[64] Yumitori S. J Mater Sci, 2000, 35: 139

Low-temperature graphitization of amorphous carbon nanospheres

Low-temperature graphitization of amorphous carbon nanospheres

PDF

可视化

摘要/Abstract

引用本文

使用本文

扫码分享

参考文献

相关文章 0

编辑推荐

Metrics