高活性甲醇氧化电催化剂Pt-Pd纳米合金的组分可控合成

doi:10.1016/S1872-2067(18)63020-7

催化学报 ›› 2018, Vol. 39 ›› Issue (2): 342-349.DOI: 10.1016/S1872-2067(18)63020-7

• 论文 • 上一篇

高活性甲醇氧化电催化剂Pt-Pd纳米合金的组分可控合成

赵海强^a, 齐卫宏^a,b, 周鑫峰^a, 吴灏斐^a, 李业军^c

a 中南大学材料科学与工程学院, 湖南长沙 410083;
b 中南大学教育部有色金属材料科学与工程重点实验室, 湖南长沙 410083;
c 中南大学物理与电子学院先进材料超微结构与超快过程研究重点实验室, 湖南长沙 410083

收稿日期:2017-09-20 修回日期:2017-12-27 出版日期:2018-02-18 发布日期:2018-02-10
通讯作者: 齐卫宏
基金资助:
国家自然科学基金（21373273）.

Composition-controlled synthesis of platinum and palladium nanoalloys as highly active electrocatalysts for methanol oxidation

Haiqiang Zhao^a, Weihong Qi^a,b, Xinfeng Zhou^a, Haofei Wu^a, Yejun Li^c

a School of Materials Science and Engineering, Central South University, Changsha 410083, Hunan, China;
b Key Laboratory of Non-ferrous Materials Science and Engineering, Ministry of Education, Central South University, Changsha 410083, Hunan, China;
c Hunan Key Laboratory of Super Microstructure and Ultrafast Process, School of Physics and Electronics, Central South University, Changsha 410083, Hunan, China

Received:2017-09-20 Revised:2017-12-27 Online:2018-02-18 Published:2018-02-10
Contact: 10.1016/S1872-2067(18)63020-7
Supported by:
This work was supported by the National Natural Science Foundation of China (21373272).

摘要/Abstract

摘要：

Pt纳米粒子由于其本身独特的物理、化学性质以及能够同时促进氧化和还原反应，在工业生产和商业设备中（尤其在直接甲醇燃料电池中）广泛用作重要的电催化剂.然而，Pt作为贵金属在自然界中的含量极其稀少，价格昂贵；另外，甲醇氧化反应中产生的中间产物CO很容易市Pt纳米粒子中毒而失活.因此，迫切需要一种Pt用量少，催化性能高的材料.
一制备高活性比表面积的Pt纳米颗粒，可以有效提高Pt利用率.另外，调控纳米粒子使其裸露特定的晶面、边、角以及缺陷也能有效提升催化性能.还可以采用Pt纳米粒子结合其它金属元素形成双金属合金，如，Pt-M（M=Pd，Au，Ag，Ru，Fe，Co，Ni，等）催化剂，可以在减少Pt元素用量的同时有效提升催化活性.在众多可供选择的元素中，Pd相对于Pt价格低廉，但两者具有相近的物理、化学性质以及较高的电催化性能，使Pt-Pd纳米合金呈现十分优异的电催化性能.研究表明，Pt-Pd纳米合金在酸性和CO环境中能有效催化有机小分子电氧化过程.另外，在酸性环境中，用Pd替代Cu，Ag，Co或Ni，可以有效减少催化剂的腐蚀.
本文在乙二醇溶液中同时还原K₂PtCl₄和Na₂PdCl₄，在110℃反应5 h制备出超细的Pt-Pd纳米合金.通过X射线衍射（XRD）、透射电子显微镜（TEM）、高分辨透射电子显微镜（HRTEM）以及能谱仪（EDS）对合金进行表征，从而确定产物为尺寸4 nm左右的Pt-Pd纳米合金，且通过改变金属前驱体的投料比可以有效调控Pt-Pd合金组分（按元素比例分别表示为Pt1Pd3，Pt1Pd1，Pt3Pd1）.采用循环伏安法、线性扫描伏安法以及计时安培法等多种手段测试样品在0.5 mol/L H₂SO₄和0.5 mol/L CH₃OH的酸性环境中（50 mV/s）电化学性能，并与商业Pt/C进行比较.结果表明，合金的催化性能和组分密切相关，当Pt元素的含量为75%左右时，Pt-Pd纳米合金表现出最佳的催化活性和稳定性，其中Pt₃Pd₁的电催化质量活性可达商业Pt/C的7倍之多.我们把Pt-Pd纳米合金的催化性能对其组分的依赖性归结为甲醇氧化反应中的双官能团机制，反应中，Pt可有效催化甲醇脱氢产生Pt-CO，Pd则催化水脱氢形成Pd-OH.当Pd含量减少时，Pt表面的水脱氢反应只有在高电位才能发生，从而降低催化效率；而Pd含量过多，则会抑制Pt催化甲醇的脱氢反应，使催化效率大大降低.因此，只有适宜Pt/Pd比例，才能有效提升催化效率.

关键词: 铂钯纳米合金, 组分和尺寸可控, 甲醇氧化

Abstract:

Platinum and palladium (PtPd) alloy nanoparticles (NPs) are excellent catalysts for direct methanol fuel cells. In this study, we developed PtPd alloy NPs through the co-reduction of K₂PtCl₄ and Na₂PdCl₄ in a polyol synthesis environment. During the reaction, the feed molar ratio of the two precursors was carried over to the final products, which have a narrow size distribution with a mean size of approximately 4 nm. The catalytic activity for methanol oxidation reactions possible depends closely on the composition of as-prepared PtPd alloy NPs, and the NPs with a Pt atomic percentage of approximately 75% result in higher activity and stability with a mass specific activity that is 7 times greater than that of commercial Pt/C catalysts. The results indicate that through composition control, PtPd alloy NPs can improve the effectiveness of catalytic performance.

Key words: Platinum and palladium alloy nanoparticles, Composition and size control, Methanol oxidation

赵海强, 齐卫宏, 周鑫峰, 吴灏斐, 李业军. 高活性甲醇氧化电催化剂Pt-Pd纳米合金的组分可控合成[J]. 催化学报, 2018, 39(2): 342-349.

Haiqiang Zhao, Weihong Qi, Xinfeng Zhou, Haofei Wu, Yejun Li. Composition-controlled synthesis of platinum and palladium nanoalloys as highly active electrocatalysts for methanol oxidation[J]. Chinese Journal of Catalysis, 2018, 39(2): 342-349.

×
扫码分享

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://www.cjcatal.com/CN/10.1016/S1872-2067(18)63020-7

https://www.cjcatal.com/CN/Y2018/V39/I2/342

参考文献

[1] W. Y. Wang, D. S. Wang, X. W. Liu, Q. Peng, Y. D. Li, Chem. Com-mun., 2013, 49, 2903-2905.
[2] B. H. Wu, N. F. Zheng, G. Fu, Chem. Commun., 2011, 47, 1039.
[3] J. J. Lv, J. N. Zheng, S. S. Li, L. L. Chen, A. J. Wang, J. J. Feng, J. Mater. Chem. A, 2014, 2, 4384-4390.
[4] B. H. Zhang, Y. G. Xue, H. Sun, A. Jiang, Z. B. Li, J. C. Hao, RSC Advances, 2016, 6, 56083-56090.
[5] L. N. Zhou, X. T. Zhang, Z. H. Wang, S. J Guo, Y. J. Li, Chem. Commun., 2016, 52, 12737-12740.
[6] S. Mourdikoudis, M. Chirea, T. Altantzis, I. Pastoriza-Santos, J. Perez-Juste, F. Silva, S. Bals, L. M. Liz-Marzan, Nanoscale, 2013, 5, 4776-4784.
[7] A. C. Chen, P. Holt-Hindle, Chem. Rev., 2010, 110, 3767-3804.
[8] R. Adzic, J. Lipkowski, P. Ross, Electrocatalysis, 1998, 197-241.
[9] A. B. Anderson, Electrochimi. Acta, 2002, 47, 3759-3763.
[10] W. H. Ji, W. H. Qi, S. S. Tang, H. C. Peng, S. Q. Li, Nanomaterials, 2015, 5, 2203-2211.
[11] K.M. Bratlie, H. Lee, K. Komvopoulos, P. D. Yang, G. A. Somorjai, Nano Lett., 2007, 7, 3097-3101.
[12] C. Wang, H. Daimon, T. Onodera, T. Koda, S. Sun, Angew. Chem. Int. Ed., 2008, 47, 3588-3591.
[13] W. H, Qi, Acc. Chem. Res., 2016, 49, 1587-1595.
[14] D. Xu, Z. P. Liu, H. Z. Yang, Q. S. Liu, J. Zhang, J. Y. Fang, S. Z. Zou, K. Sun, Angew. Chem. Int. Ed., 2009, 48, 4217-4221.
[15] J. Zhang, J. Y. Fang, J. Am. Chem. Soc., 2009, 131, 18543-18547.
[16] D. S. Wang, Q. Peng, Y. D. Li, Nano Res., 2010, 3, 574-580.
[17] J. Kim, Y. Lee, S. Sun, J. Am. Chem. Soc., 2010, 132, 4996-4997.
[18] Y. J. Kang, C. B. Murray, J. Am. Chem. Soc., 2010, 132, 7568-7569.
[19] V. R. Stamenkovic, B. S. Mun, M. Arenz, K. J. J. Mayrhofer, C. A. Lucas, G. F. Wang, P. N. Ross, N. M. Markovic, Nat. Mater., 2007, 6, 241-247.
[20] C. Venkateswara Rao, B. Viswanathan, J. Phys. Chem. C, 2009, 113, 18907-18913.
[21] F. Kadirgan, S. Beyhan, T. Atilan, Int. J. Hydrogen Energy, 2009, 34, 4312-4320.
[22] Q. Yuan, Z. Y. Zhou, J. Zhuang, X. Wang, Chem. Commun., 2010, 46, 1491-1493.
[23] H. Yasuda, N. Matsubayashi, T. Sato, Y. Yoshimura, Cataly. Let-t., 1998, 54, 23-27.
[24] E. Antolini, Energy Environ. Sci., 2009, 2, 915-931.
[25] V. R. Stamenkovic, B. S. Fowler, B. S. Mun, G. F. Wang, P. N. Ross, C. A. Lucas, N. M. Markovic, Science, 2007, 315, 493-497.
[26] H. Ataee-Esfahani, M. Imura, Y. Yamauchi, Angew. Chem. Int. Ed., 2013, 125, 13856-13860.
[27] L. Wang, Y. Yamauchi, J. Am. Chem. Soc., 2013, 135, 16762-16765.
[28] A. X. Yin, X. Q. Min, Y. W. Zhang, C. H. Yan, J. Am. Chem. Soc., 2011, 133, 3816-3819.
[29] W. Liu, P. Rodriguez, L. Borchardt, A. Foelske, J. Yuan, A. K. Herrmann, D. Geiger, Z. K. Zheng, S. Kaskel, N. Gaponik, R. Kötz, T. J. Schmidt, A. Eychmüller, Angew. Chem. Int. Ed., 2013, 52, 9849-9852.
[30] B. Lim, M. Jiang, P. H. C. Camargo, E. C. Cho, J. Tao, X. M. Lu, Y. M. Zhu, Y. N. Xia, Science, 2009, 324, 1302-1305.
[31] I. Choi, S. H. Ahn, J. J. Kim, O. J. Kwon, Appl. Catal. B, 2011, 102, 608-613.
[32] C. Koenigsmann, A. C. Santulli, K. Gong, M. B. Vukmirovic, W. P. Zhou, E. Sutter, S. S. Wong, R. R. Adzic, J. Am. Chem. Soc., 2011, 133, 9783-9795.
[33] I. Washio, Y. J. Xiong, Y. D. Yin, Y. N. Xia, Adv. Mater., 2006, 18, 1745-1749.
[34] S. E. Skrabalak, B. J. Wiley, M. Kim, E.V. Formo, Y. N. Xia, Nano Lett., 2008, 8, 2077-2081.
[35] S. E. Skrabalak, J. Y. Chen, Y. G. Sun, X. M. Lu, L. Au, C.M. Cobley, Y. N. Xia, Acc. Chem. Res., 2008, 41, 1587-1595.
[36] Y. J. Xiong, H. G. Cai, B. J. Wiley, J. G. Wang, M. J. Kim, Y. N. Xia, J. Am. Chem. Soc., 2007, 129, 3665-3675.
[37] A. Mohanty, N. Garg, R. C. Jin, Angew. Chem., 2010, 49, 4962-4966.
[38] B. Neppolian, V. Sáez, J. González-García, F. Grieser, R. Gómez, M. Ashokkumar, J. Solid State Electrochem., 2014, 18, 3163-3171.
[39] S. Chen, P. J. Ferreira, W. C. Sheng, N. Yabuuchi, L. F. Allard, S. H. Yang, J. Am. Chem. Soc., 2008, 130, 13818-13819.
[40] S. I. Sanchez, M. W. Small, J. M. Zuo, R. G. Nuzzo, J. Am. Chem. Soc., 2009, 131, 8683-8689.
[41] F. R. De. Boer, R. Boom, W. C. M. Mattens, A. R. Miedema, A. K. Niessen, in Metals:Transition Metal Alloys, 1988.
[42] K. D. Gilroy, A. Ruditskiy, H. C. Peng, D. Qin, Y. N. Xia, Chem Rev., 2016, 116, 10414-10472.
[43] M. Watanabe, M. Tomikawa, S. Motoo, J. Electroanal. Chem. Interface., 1985, 195, 81-93.
[44] Y. Liu, M. Chi, V. Mazumder, K. L. More, S. Soled, J. D. Henao, S. H. Sun, Chem. Mater., 2011, 23, 4199-4203.
[45] C. R. Anthony, L. McElwee-White, J. Am. Chem. Soc., 2006, 921, 130-142.
[46] H. A. Gasteiger, S. S. Kocha, B. Sompalli, F. T. Wagner, Appl. Catal. B, 2005, 56, 9-35.
[47] F. Liu, J. Y. Lee, W. J. Zhou, Small, 2006, 2, 121-128.

高活性甲醇氧化电催化剂Pt-Pd纳米合金的组分可控合成

Composition-controlled synthesis of platinum and palladium nanoalloys as highly active electrocatalysts for methanol oxidation

PDF

Supporting Information

可视化

摘要/Abstract

引用本文

使用本文

扫码分享

参考文献

相关文章 15

编辑推荐

Metrics

[1]	孙丽娟, 于晓慧, 唐丽永, 王伟康, 刘芹芹. 构建K₃PW₁₂O₄₀/CdS核壳S型异质结实现同步太阳能光催化分解水和选择性苯甲醇氧化反应[J]. 催化学报, 2023, 52(9): 164-175.
[2]	孙利娟, 王伟康, 路平, 刘芹芹, 王乐乐, 唐华. 纳米高熵合金实现光催化剂肖特基势垒的调控用于光催化制氢与苯甲醇氧化耦合反应[J]. 催化学报, 2023, 51(8): 90-100.
[3]	魏英聪, 张琪琪, 周颖, 马雄风, 王乐乐, 王严杰, 洒荣建, 龙金林, 付贤智, 员汝胜. 非贵金属等离子共振增强MoO_3-_x基S型异质结光催化苯甲醇氧化同步产氢和苯甲醛[J]. 催化学报, 2022, 43(10): 2665-2677.
[4]	陈军伟, 欧祖翘, 陈海鑫, 宋树芹, 王昆, 王毅. 电催化剂纳米碳基载体的研究进展[J]. 催化学报, 2021, 42(8): 1297-1326.
[5]	钟静萍, 黄科薪, 许文涛, 唐华果, Muhammad Waqas, 樊友军, 王睿翔, 陈卫, 王沂轩. 导电共聚物衍化新策略制备硫、氮共掺杂碳纳米管及其对改善PtCu纳米晶分散性与甲醇电催化氧化的促进作用[J]. 催化学报, 2021, 42(7): 1205-1215.
[6]	李石波, 田植群, 刘洋, 蒋政, 哈森, 陈兴发, 帕纳斯, 沈培康. 分级骨架和多层的Pt-Ni纳米晶体用于高效氧还原和甲醇氧化反应[J]. 催化学报, 2021, 42(4): 648-657.
[7]	刘建芳, 冉真真, 曹琪岩, 季生福. MIL-88B(Fe_x, Co_1‒_x)催化剂制备及甲醇液相H₂O₂氧化一步合成甲酸甲酯[J]. 催化学报, 2021, 42(12): 2254-2264.
[8]	Hee Jin Kim, Yong-Deok Ahn, Jeonghyeon Kim, Kyoung-Su Kim, Yeon Uk Jeong, Jong Wook Hong, Sang-Il Choi. Pt-Pb六边形纳米板电催化甲醇氧化反应中的表面元素分布效应[J]. 催化学报, 2020, 41(5): 813-819.
[9]	杨军, 刘雨溪, 邓积光, 赵星天, 张昆锋, 韩卓, 戴洪兴. AgAuPd/meso-Co₃O₄高效甲醇氧化催化剂[J]. 催化学报, 2019, 40(6): 837-848.
[10]	蒋湘芬, 王学斌, 沈丽明, 吴强, 王秧年, 马延文, 王喜章, 胡征. 分级结构氮掺杂碳纳米笼担载的铂基高效甲醇氧化电催化剂[J]. 催化学报, 2016, 37(7): 1149-1155.
[11]	施梅勤, 章文天, 李影影, 褚有群, 马淳安. 碳化钨-石墨烯插层复合物的制备及作为甲醇氧化助催化剂的性能研究[J]. 催化学报, 2016, 37(11): 1851-1859.
[12]	洪锦德, 刘子豪, 维拉库玛, 吴培豪, 刘端祺, 刘尚斌. 用于燃料电池阳极的有序介孔碳负载的双功能Pt-M(M=Ru,Fe,Mo)电催化剂[J]. 催化学报, 2016, 37(1): 43-53.
[13]	Mahesh M. Nair, Freddy Kleitz, Serge Kaliaguine. 孔结构对纳米浇注的中孔钙钛矿上甲醇氧化反应动力学的影响[J]. 催化学报, 2016, 37(1): 32-42.
[14]	伍颖斯, 余皓, 王红娟, 彭峰. 石墨烯负载的金属氧化物纳米颗粒的可控制备及催化性能[J]. 催化学报, 2014, 35(6): 952-959.
[15]	张洁, 唐水花, 廖龙渝, 郁卫飞. 低温燃料电池非铂催化剂研究进展[J]. 催化学报, 2013, 34(6): 1051-1065.