重构法合成Cu-SAPO-34及其NH3-SCR催化性能

doi:10.1016/S1872-2067(20)63583-5

催化学报 ›› 2020, Vol. 41 ›› Issue (9): 1410-1420.DOI: 10.1016/S1872-2067(20)63583-5

重构法合成Cu-SAPO-34及其NH₃-SCR催化性能

孙丽婧^a,b, 杨淼^a, 曹毅^a,c, 田鹏^a, 吴鹏飞^a,b, 曹磊^a, 徐舒涛^a, 曾姝^a,b, 刘中民^a

a 中国科学院大连化学物理研究所, 洁净能源国家实验室(筹), 甲醇制烯烃国家工程实验室, 辽宁大连 116023;
b 中国科学院大学, 北京 100049;
c 宁波大学材料科学与化学工程学院, 浙江宁波 315211

收稿日期:2020-01-16 修回日期:2020-02-27 出版日期:2020-09-18 发布日期:2020-08-08
通讯作者: 田鹏, 刘中民
基金资助:
国家自然科学基金（21476228，21606221，21676262，21991091），中国科学院前沿科学重点研究计划（QYZDB-SSW-JSC0 40）.

A reconstruction strategy for the synthesis of Cu-SAPO-34 with excellent NH₃-SCR catalytic performance and hydrothermal stability

Lijing Sun^a,b, Miao Yang^a, Yi Cao^a,c, Peng Tian^a, Pengfei Wu^a,b, Lei Cao^a, Shutao Xu^a, Shu Zeng^a,b, Zhongmin Liu^a

a National Engineering Laboratory for Methanol to Olefins, Dalian Institute of Chemical Physics, Chinese Academy of Sciences, Dalian 116023, Liaoning, China;
b University of Chinese Academy of Sciences, Beijing 100049, China;
c School of Material Science and Chemical Engineering, Ningbo University, Ningbo 315211, Zhejiang, China

Received:2020-01-16 Revised:2020-02-27 Online:2020-09-18 Published:2020-08-08
Supported by:
This work was supported by the National Natural Science Foundation of China (21476228, 21606221, 21676262, 21991091), and the Key Research Program of Frontier Sciences, CAS (QYZDB-SSW-JSC0 40).

摘要/Abstract

摘要： 氨选择催化还原NO_x（NH₃-SCR）是重要的柴油车尾气脱硝技术.发展高效且稳定的催化剂是提升该技术指标、应对严苛排放标准的关键.近年来，以Cu-SSZ-13和Cu-SAPO-34为代表的金属离子负载分子筛催化剂材料因其较宽的活性温度窗口和高水热稳定性受到研究者的广泛关注.Cu-SSZ-13分子筛催化剂已被BASF公司商业应用.相较Cu-SSZ-13，Cu-SAPO-34具有更优的低温活性与高温水热稳定性，且合成成本低廉.但Cu-SAPO-34的低温耐水性差，当采用传统的金属离子负载过程进行反复多次离子交换时，存在分子筛结晶度下降（部分骨架结构塌陷）的风险.使用铜四乙烯五胺络合物（Cu-TEPA）作为模板剂和铜源一步合成Cu-SAPO-34可以避免反复的离子交换过程，但由于Cu-TEPA的模板导向能力过强，Cu负载量难以控制，而降低Cu-TEPA的投料量则会损失产品收率.同时，该方法合成的Cu-SAPO-34中含有大量硅岛，分子筛催化剂的水热稳定性显著降低.针对这些问题，本文提出利用一步合成的高铜含量Cu-SAPO-34作为前驱体与铜源合成Cu-SAPO-34的方法（命名为重构法）.该方法不仅产品收率高，而且Cu和Si的含量/分布可控，合成样品的NH₃-SCR催化性能和水热稳定性也明显提升.
EDX结果显示，焙烧后的Cu-SAPO-34中铜分布均匀，说明前驱体充分参与了Cu-SAPO-34的重构.¹³C NMR和元素分析结果显示，相较一步法合成的Cu-SAPO-34，重构的Cu-SAPO-34中的四乙烯五胺在模板剂中的比例明显下降.Cu-TEPA限域在前驱体的CHA笼中，有效抑制其结构导向剂的作用.Cu引入量由前驱体加入量决定.²⁹Si NMR结果显示，Cu-SAPO-34中的硅主要呈Si（4Al）分布，这有利于Cu-SAPO-34保持良好的高温水热稳定性.NH₃-SCR反应结果显示，相较一步法合成的Cu-SAPO-34，重构的Cu-SAPO-34表现出良好的NH₃-SCR反应活性和更优异的高温水热稳定性.不同硅含量的重构Cu-SAPO-34的NH₃-SCR反应结果显示：在低温段，低硅含量的Cu-SAPO-34具有更高的反应活性；在高温段，高硅含量的Cu-SAPO-34具有更高的反应活性.通过NH₃-TPD和原位红外漫反射分析发现，低硅含量的Cu-SAPO-34具有相对较弱的酸性，使得吸附的氨具有较高的反应性，催化剂的低温活性较高.

关键词: Cu-SAPO-34, 水热合成, NH₃-SCR, 水热稳定性, 晶化

Abstract: A reconstruction strategy has been developed to synthesize Cu-SAPO-34 with a wide crystallization phase region, high solid yield, and tunable Si and Cu contents. Cu-rich SAPO-34 was prepared from a Cu-amine complex, which acted as a precursor and Cu source for the reconstruction synthesis. The role of the Cu-amine complex as a template was restricted, which allowed easier control over the Cu and Si contents than in the previously reported "one-pot" synthesis method. Characterization of the material revealed that the Si(4Al) coordination environment dominates the synthesized Cu-SAPO-34 catalysts. High-temperature hydrothermal treatment increased the isolated Cu²⁺ content slightly, and the acid sites in the low-silica catalyst are more resistant to hydrothermal treatment than those of the existing catalysts. The obtained materials, especially the low-silica Cu-SAPO-34 sample, exhibit excellent catalytic activity and hydrothermal stability for the selective catalytic reduction of NO_x by NH₃ (NH₃-SCR). In addition, the influence of the catalyst acidity on the NH₃-SCR reaction was also investigated and is discussed. The high synthetic efficiency and outstanding catalytic performance make Cu-SAPO-34 synthesized by the reconstruction method a promising catalyst for the NH₃-SCR process.

Key words: Cu-SAPO-34, Hydrothermal synthesis, NH₃-SCR, Hydrothermal stability, Crystallization

孙丽婧, 杨淼, 曹毅, 田鹏, 吴鹏飞, 曹磊, 徐舒涛, 曾姝, 刘中民. 重构法合成Cu-SAPO-34及其NH₃-SCR催化性能[J]. 催化学报, 2020, 41(9): 1410-1420.

Lijing Sun, Miao Yang, Yi Cao, Peng Tian, Pengfei Wu, Lei Cao, Shutao Xu, Shu Zeng, Zhongmin Liu. A reconstruction strategy for the synthesis of Cu-SAPO-34 with excellent NH₃-SCR catalytic performance and hydrothermal stability[J]. Chinese Journal of Catalysis, 2020, 41(9): 1410-1420.

×
扫码分享

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://www.cjcatal.com/CN/10.1016/S1872-2067(20)63583-5

https://www.cjcatal.com/CN/Y2020/V41/I9/1410

参考文献

[1] E. Borfecchia, P. Beato, S. Svelle, U. Olsbye, C. Lamberti, S. Bordiga, Chem. Soc. Rev., 2018, 47, 8097-8133.
[2] P. Granger, V. I. Parvulescu, Chem. Rev., 2011, 111, 3155-3207.
[3] S. C. Anenberg, J. Miller, R. M. Injares, L. Du, D. K. Henze, F. Lacey, C. S. Malley, L. Emberson, V. Franco, Z. Klimont, C. Heyes, Nature, 2017, 545, 467-471.
[4] Y. Xin, Q. Li, Z. Zhang, ChemCatChem, 2018, 10, 29-41.
[5] A. M. Beale, F. Gao, I. Lezcano-Gonzalez, C. H. F. Peden, J. Szanyi, Chem. Soc. Rev., 2015, 44, 7371-7405.
[6] Y. J. Li, W. K. Hall, J. Catal., 1991, 129, 202-215.
[7] J. Wang, H. Zhao, G. Haller, Y. Li, Appl.Catal. B-Environ., 2017, 202, 346-354.
[8] I. Bull, W. M. Xue, P. Burk, R. S. Boorse, W. M. Jaglowski, G. S. Koermer, A. Moini, J. A. Patchett, J. C. Dettling, M. T. Caudle, US Patent 7601662, 2009.
[9] P. J. Andersen, J. E. Bailie, J. L. Casci, H. Y. Chen, J. M. Fedeyko, R. K. S. Foo, R. R. Rajaram, WO Patent, 132452, 2008.
[10] D. W. Fickel, E. D'Addio, J. A. Lauterbach, R. F. Lobo, Appl.Catal. B-Environ., 2011, 102, 441-448.
[11] D. Wang, Y. Jangjou, Y. Liu, M. K. Sharma, J. Luo, J. Li, K. Kamasamudram, W. S. Epling, Appl. Catal. B-Environ., 2015, 165, 438-445.
[12] L. Ma, Y. Cheng, G. Cavataio, R. W. McCabe, L. Fu, J. Li, Chem. Eng. J., 2013, 225, 323-330.
[13] F. Gao, E. D. Walter, N. M. Washton, J. Szanyi, C. H. F. Peden, ACS Catal., 2013, 3, 2083-2093.
[14] J. Fan, P. Ning, Y. Wang, Z. Song, X. Liu, H. Wang, J. Wang, L. Wang, Q. Zhang, Chem. Eng. J., 2019, 369, 908-919.
[15] Y. Cao, S. Zou, L. Lan, Z. Yang, H. Xu, T. Lin, M. Gong, Y. Chen, J. Mol. Catal. A-Chem., 2015, 398, 304-311.
[16] X. Xiang, M. Yang, B. Gao, Y. Qiao, P. Tian, S. Xu, Z. Liu, RSC Adv., 2016, 6, 12544-12552.
[17] F. Gao, E. D. Walter, N. M. Washton, J. Szanyi, C. H. F. Peden, Appl. Catal. B-Environ., 2015, 162, 501-514.
[18] L. M. Ren, L. F. Zhu, C. G. Yang, Y. M. Chen, Q. Sun, H. Y. Zhang, C. J. Li, F. Nawaz, X. J. Meng, F. S. Xiao, Chem. Commun., 2011, 47, 9789-9791.
[19] R. Martinez-Franco, M. Moliner, C. Franch, A. Kustov, A. Corma, Appl. Catal. B-Environ., 2012, 127, 273-280.
[20] A. Turrina, E. C. V. Eschenroeder, B. E. Bode, J. E. Collier, D. C. Apperley, P. A. Cox, J. L. Casci, P. A. Wright, Microporous Mesoporous Mater., 2015, 215, 154-167.
[21] R. Martinez-Franco, M. Moliner, P. Concepcion, J. R. Thogersen, A. Corma, J. Catal., 2014, 314, 73-82.
[22] L. Wang, W. Li, S. J. Schmieg, D. Weng, J. Catal., 2015, 324, 98-106.
[23] D. Fan, P. Tian, S. Xu, Q. Xia, X. Su, L. Zhang, Y. Zhang, Y. He, Z. Liu, J. Mater. Chem., 2012, 22, 6568-6574.
[24] C. Pellegrino, R. Aiello, F. Testa, F. Crea, A. Tuel, J. B. Nagy, Microporous Mesoporous Mater., 2001, 47, 85-96.
[25] D. Wang, P. Tian, M. Yang, S. Xu, D. Fan, X. Su, Y. Yang,C. Wang, Z. Liu, Microporous Mesoporous Mater., 2014, 194, 8-14.
[26] G. Liu, P. Tian, Z. Liu, Chin. J. Catal., 2012, 33, 174-182.
[27] X. Xiang, P. Wu, Y. Cao, L. Cao, Q. Wang, S. Xu, P. Tian, Z. Liu, Chin. J. Catal., 2017, 38, 918-927.
[28] Y. Cao, D. Fan, P. Tian, L. Cao, T. Sun, S. Xu, M. Yang, Z. Liu, Chem. Eng. J., 2018, 354, 85-92.
[29] Z. Chen, C. Fan, L. Pang, S. Ming, W. Guo, P. Liu, H. Chen, T. Li, Chem. Eng. J., 2018, 348, 608-617.
[30] L. Wang, W. Li, G. Qi, D. Weng, J. Catal., 2012, 289, 21-29.
[31] D. Wang, L. Zhang, K. Kamasamudram, W. S. Epling, ACS Catal., 2013, 3, 871-881.
[32] T. Yu, D. Fan, T. Hao, J. Wang, M. Shen, W. Li, Chem. Eng. J., 2014, 243, 159-168.
[33] T. Yu, J. Wang, M. Q. Shen, W. Li, Catal. Sci. Technol., 2013, 3, 3234-3241.
[34] J. Wang, D. Fan, T. Yu, J. Wang, T. Hao, X. Hu, M. Shen, W. Li, J. Catal., 2015, 322, 84-90.
[35] J. Zhong, J. Han, Y. Wei, S. Xu, T. Sun, X. Guo, C. Song, Z. Liu, Chin. J. Catal., 2018, 39, 1821-1831.
[36] S. K. Fan, J. J. Xue, T. Yu, D. Q. Fan, T. Hao, M. Q. Shen, W. Li, Catal. Sci. Technol., 2013, 3, 2357-2364.
[37] Y. Wan, J. X. Ma, Z. Wang, W. Zhou, S. Kaliaguine, J. Catal., 2004, 227, 242-252.
[38] L. Wang, J. R. Gaudet, W. Li, D. Weng, J. Catal., 2013, 306, 68-77.
[39] X. L. Shan, N. J. Guan, X. Zeng, J. X. Chen, S. H. Xiang, Chin. J. Catal., 2001, 22, 237-241.iron., 2017, 202, 346-354.
[8] I. Bull, W. M. Xue, P. Burk, R. S. Boorse, W. M. Jaglowski, G. S. Koermer, A. Moini, J. A. Patchett, J. C. Dettling, M. T. Caudle, US Patent 7601662, 2009.
[9] P. J. Andersen, J. E. Bailie, J. L. Casci, H. Y. Chen, J. M. Fedeyko, R. K. S. Foo, R. R. Rajaram, WO Patent, 132452, 2008.
[10] D. W. Fickel, E. D'Addio, J. A. Lauterbach, R. F. Lobo, Appl.Catal. B-Environ., 2011, 102, 441-448.
[11] D. Wang, Y. Jangjou, Y. Liu, M. K. Sharma, J. Luo, J. Li, K. Kamasam-udram, W. S. Epling, Appl. Catal. B-Environ., 2015, 165, 438-445.
[12] L. Ma, Y. Cheng, G. Cavataio, R. W. McCabe, L. Fu, J. Li, Chem. Eng. J., 2013, 225, 323-330.
[13] F. Gao, E. D. Walter, N. M. Washton, J. Szanyi, C. H. F. Peden, ACS Catal., 2013, 3, 2083-2093.
[14] J. Fan, P. Ning, Y. Wang, Z. Song, X. Liu, H. Wang, J. Wang, L. Wang, Q. Zhang, Chem. Eng. J., 2019, 369, 908-919.
[15] Y. Cao, S. Zou, L. Lan, Z. Yang, H. Xu, T. Lin, M. Gong, Y. Chen, J. Mol. Catal. A-Chem., 2015, 398, 304-311.
[16] X. Xiang, M. Yang, B. Gao, Y. Qiao, P. Tian, S. Xu, Z. Liu, RSC Adv., 2016, 6, 12544-12552.
[17] F. Gao, E. D. Walter, N. M. Washton, J. Szanyi, C. H. F. Peden, Appl. Catal. B-Environ., 2015, 162, 501-514.
[18] L. M. Ren, L. F. Zhu, C. G. Yang, Y. M. Chen, Q. Sun, H. Y. Zhang, C. J. Li, F. Nawaz, X. J. Meng, F. S. Xiao, Chem. Commun., 2011, 47, 9789-9791.
[19] R. Martinez-Franco, M. Moliner, C. Franch, A. Kustov, A. Corma, Appl. Catal. B-Environ., 2012, 127, 273-280.
[20] A. Turrina, E. C. V. Eschenroeder, B. E. Bode, J. E. Collier, D. C. Apperley, P. A. Cox, J. L. Casci, P. A. Wright, Microporous Mesoporous Mater., 2015, 215, 154-167.
[21] R. Martinez-Franco, M. Moliner, P. Concepcion, J. R. Thogersen, A. Corma, J. Catal., 2014, 314, 73-82.
[22] L. Wang, W. Li, S. J. Schmieg, D. Weng, J. Catal., 2015, 324, 98-106.
[23] D. Fan, P. Tian, S. Xu, Q. Xia, X. Su, L. Zhang, Y. Zhang, Y. He, Z. Liu, J. Mater. Chem., 2012, 22, 6568-6574.
[24] C. Pellegrino, R. Aiello, F. Testa, F. Crea, A. Tuel, J. B. Nagy, Mi-croporous Mesoporous Mater., 2001, 47, 85-96.
[25] D. Wang, P. Tian, M. Yang, S. Xu, D. Fan, X. Su, Y. Yang,C. Wang, Z. Liu, Microporous Mesoporous Mater., 2014, 194, 8-14.
[26] G. Liu, P. Tian, Z. Liu, Chin. J. Catal., 2012, 33, 174-182.
[27] X. Xiang, P. Wu, Y. Cao, L. Cao, Q. Wang, S. Xu, P. Tian, Z. Liu, Chin. J. Catal., 2017, 38, 918-927.
[28] Y. Cao, D. Fan, P. Tian, L. Cao, T. Sun, S. Xu, M. Yang, Z. Liu, Chem. Eng. J., 2018, 354, 85-92.
[29] Z. Chen, C. Fan, L. Pang, S. Ming, W. Guo, P. Liu, H. Chen, T. Li, Chem. Eng. J., 2018, 348, 608-617.
[30] L. Wang, W. Li, G. Qi, D. Weng, J. Catal., 2012, 289, 21-29.
[31] D. Wang, L. Zhang, K. Kamasamudram, W. S. Epling, ACS Catal., 2013, 3, 871-881.
[32] T. Yu, D. Fan, T. Hao, J. Wang, M. Shen, W. Li, Chem. Eng. J., 2014, 243, 159-168.
[33] T. Yu, J. Wang, M. Q. Shen, W. Li, Catal. Sci. Technol., 2013, 3, 3234-3241.
[34] J. Wang, D. Fan, T. Yu, J. Wang, T. Hao, X. Hu, M. Shen, W. Li, J. Catal., 2015, 322, 84-90.
[35] J. Zhong, J. Han, Y. Wei, S. Xu, T. Sun, X. Guo, C. Song, Z. Liu, Chin. J. Catal., 2018, 39, 1821-1831.
[36] S. K. Fan, J. J. Xue, T. Yu, D. Q. Fan, T. Hao, M. Q. Shen, W. Li, Catal. Sci. Technol., 2013, 3, 2357-2364.
[37] Y. Wan, J. X. Ma, Z. Wang, W. Zhou, S. Kaliaguine, J. Catal., 2004, 227, 242-252.
[38] L. Wang, J. R. Gaudet, W. Li, D. Weng, J. Catal., 2013, 306, 68-77.
[39] X. L. Shan, N. J. Guan, X. Zeng, J. X. Chen, S. H. Xiang, Chin. J. Catal., 2001, 22, 237-241.

重构法合成Cu-SAPO-34及其NH₃-SCR催化性能

A reconstruction strategy for the synthesis of Cu-SAPO-34 with excellent NH₃-SCR catalytic performance and hydrothermal stability

PDF

Supporting Information

可视化

摘要/Abstract

引用本文

使用本文

扫码分享

参考文献

相关文章 15

编辑推荐

Metrics

[1]	赵彬彬, 钟威, 陈峰, 王苹, 别传彪, 余火根. 高晶化g-C₃N₄光催化剂: 合成、结构调控和光催化产氢[J]. 催化学报, 2023, 52(9): 127-143.
[2]	程蕾, 张鹏, 文岐业, 范佳杰, 向全军. 铜铂双单原子负载晶化氮化碳及其增强光催化CO₂还原性能[J]. 催化学报, 2022, 43(2): 451-460.
[3]	尹金鹏, 金鑫, 徐浩, 关业军, 彭如斯, 陈丽, 蒋金刚, 吴鹏. 富硅壳层结构的无粘结剂MWW钛硅分子筛用作高选择性、高稳定性的丙烯环氧化[J]. 催化学报, 2021, 42(9): 1561-1575.
[4]	刘晓玲, 陈磊, 许红中, 蒋师, 周瑜, 王军. 直接合成Beta沸石封装Pt纳米粒子用于5-羟甲基糠醛合成2,5-呋喃二甲酸[J]. 催化学报, 2021, 42(6): 994-1003.
[5]	李阳, 张岱南, 范佳杰, 向全军. 高结晶氮化碳空心球的制备及其增强光催化产氢活性[J]. 催化学报, 2021, 42(4): 627-636.
[6]	刘晓娜, 曹毅, 闫娜娜, 马超, 曹磊, 郭鹏, 田鹏, 刘中民. Cu-SAPO-17:一种新颖的NO_x选择性催化还原催化剂[J]. 催化学报, 2020, 41(11): 1715-1722.
[7]	李阳, 张岱南, 冯雄汉, 向全军. 盐酸处理制备高结晶氮化碳及其增强光催化产氢活性[J]. 催化学报, 2020, 41(1): 21-30.
[8]	章芬, 章凌, 杨志超, 韩世超, 朱秋艳, 王亮, 刘晨光, 孟祥举, 肖丰收. 高温快速合成纳米MAZ分子筛[J]. 催化学报, 2019, 40(7): 1093-1099.
[9]	潘会严, 陈小伟, Oihane Sanz, Miguel A. Cauqui, Jose M. Rodríguez-Izquierdo, Juan J. Delgado. 一步水热法有效调变锰钾矿中钾含量及其对锰钾矿催化剂氧化还原性和催化性能的影响[J]. 催化学报, 2019, 40(6): 940-952.
[10]	张泽树, 李经纬, 易婷, 孙立伟, 张一波, 胡学风, 崔文浩, 杨向光. 调控尖晶石Co³⁺和Ni³⁺表面密度来提高催化甲烷氧化活性[J]. 催化学报, 2018, 39(7): 1228-1239.
[11]	赵孟莉, 王婉妮, 黄辰曦, 董旺, 汪洋, 程盛, 王慧庆, 钱海生. 近红外光驱动的UCNPs/Zn_xCd_1-xS纳米复合结构的化学合成并用于光化学还原六价铬[J]. 催化学报, 2018, 39(7): 1240-1248.
[12]	赵爽, 黄黎明, 江博琼, 程敏, 张嘉威, 胡一静. 分子筛负载Cu-Mn双金属柴油机尾气脱硝催化剂的稳定性[J]. 催化学报, 2018, 39(4): 800-809.
[13]	周超, 施润, 尚露, 吴骊珠, 佟振合, 张铁锐. 两步水热法合成Sn₂Nb₂O₇纳米晶及其高效可见光分解水制氢性能[J]. 催化学报, 2018, 39(3): 395-400.
[14]	周调云, 苑青, 潘秀莲, 包信和. 碳化硅上生长Cu/SSZ-13分子筛及其NH₃-SCR催化性能[J]. 催化学报, 2018, 39(1): 71-78.
[15]	向骁, 吴鹏飞, 曹毅, 曹磊, 王全义, 徐舒涛, 田鹏, 刘中民. Cu-SAPO-34催化剂的低温水热稳定性及其对NH₃选择催化还原NO_x反应性能的影响[J]. 催化学报, 2017, 38(5): 918-927.