自支撑Ni(OH)2/NF催化剂高效电催化氧化5-羟甲基糠醛反应研究

doi:10.1016/S1872-2067(24)60089-6

催化学报

自支撑Ni(OH)₂/NF催化剂高效电催化氧化5-羟甲基糠醛反应研究

霍韵滢^a,1, 郭聪^a,1, 张永乐^a, 刘婧怡^a, 张巧^a,*, 刘芝婷^a, 杨光星^a, 李仁贵^b,*, 彭峰^a,*

^a广州大学化学化工学院, 广东广州 510006;
^b中国科学院大连化学物理研究所, 大连洁净能源国家实验室, 催化基础国家重点实验室, 辽宁大连 116023

收稿日期:2024-06-10 接受日期:2024-06-10
通讯作者: * 电子信箱: zhangqiao@gzhu.edu.cn (张巧), rgli@dicp.acn.cn (李仁贵), fpeng@gzhu.edu.cn (彭峰).
作者简介:¹共同第一作者.
基金资助:
中国国家自然科学基金(51706231); 广州市自然科学基金(202201020090); 大连化学物理研究所催化基础国家重点实验室基金(N-22-10号).

Realizing efficient electrochemical oxidation of 5-hydroxymethylfurfural on a freestanding Ni(OH)₂/nickel foam catalyst

Yunying Huo^a,1, Cong Guo^a,1, Yongle Zhang^a, Jingyi Liu^a, Qiao Zhang^a,*, Zhiting Liu^a, Guangxing Yang^a, Rengui Li^b,*, Feng Peng^a,*

^aSchool of Chemistry and Chemical Engineering, Guangzhou University, Guangzhou 510006, Guangdong, China;
^bState Key Laboratory of Catalysis, Dalian National Laboratory for Clean Energy, Dalian Institute of Chemical Physics, Chinese Academy of Sciences, Dalian 116023, Liaoning, China

Received:2024-06-10 Accepted:2024-06-10
Contact: * E-mail: zhangqiao@gzhu.edu.cn (Q. Zhang), rgli@dicp.acn.cn (R. Li), fpeng@gzhu.edu.cn (F. Peng).
About author:¹Contributed equally to this work.
Supported by:
National Natural Science Foundation of China (51706231), the Natural Science Foundation of Guangzhou City (202201020090), the financial support from Supported by the fund of the State Key Laboratory of Catalysis in DICP (N-22-10).

摘要/Abstract

摘要： 随着太阳能发电能力的不断提高, 如何有效利用可再生太阳能产生的电能对生物质进行电化学转化是一个研究热点. 5-羟甲基糠醛(HMF)通过电化学实验转化为生物燃料和高附加值的含氧化学品, 为将可再生电力转化为化学品提供了一条有前途的替代途径. HMF的电催化氧化过程可以产生多种有价值的化学产品, 包括2,5-二甲酰呋喃、5-羟甲基-2-呋喃甲酸、5-甲酰-2-呋喃甲酸和2.5-呋喃二甲酸(FDCA). 其中, FDCA是生物基聚合物如聚乙烯呋喃酸酯的关键单体, 展现出取代石油衍生的聚对苯二甲酸乙二醇酯的潜力. 虽然镍基催化剂广泛应用于HMF电催化氧化反应, 但其相对较差的导电性和稳定性仍然限制了其潜在的应用.
本文报道了新颖的酸腐蚀诱导策略, 原位构建了自支撑式Ni(OH)₂/NF电极, 研究了腐蚀溶液的浓度和酸蚀时间对泡沫镍电催化氧化HMF性能的影响. 结果表明, 较高的酸浓度和较长的酸蚀时间有利于HMF电化学氧化反应. 酸诱导刻蚀Ni(OH)₂/NF电催化剂表现出稳定、高效的电化学氧化HMF性能, HMF转化率接近100%, FDCA产率与法拉第效率都在90%左右, 催化剂具有良好的稳定性, 连续5次电解循环的Ni(OH)₂/NF催化活性仍然保持稳定. 原位形成策略使Ni(OH)₂与NF之间形成致密的界面, 有助于在电化学反应中保持良好的导电性和稳定性. 原位电化学阻抗测试、原位拉曼和开路电位测试结果表明, 较好的催化性能得益于Ni(OH)₂在HMF氧化过程中动态循环演化为NiOOH, 而HMF分子迅速消耗原位形成的NiOOH物种, 生成FDCA, 同时NiOOH在此过程中被还原为最初的Ni(OH)₂. 将反应体系扩展于连续流动电解池装置, 探究了流速、电压对HMF电化学流动池反应体系的影响, 在流速为80 r min^-1, 电位为1.65 V (vs. RHE)条件下, 该装置能够稳定运行60 h, FDCA的产率高达27 mg h^-1cm^-2, 表现出较好的应用潜力.
综上, 本文提供了一种简单、经济、可扩展的设计策略, 利用酸腐蚀诱导策略在泡沫镍上原位构建出Ni(OH)₂催化剂并应用于电催化氧化HMF反应中, 探索了镍基催化剂电催化氧化HMF性能, 实现了HMF分子的高效转化, 同时将其扩展于小型连续流动电解池体系, 为HMF电化学工业化提供可能性.

关键词: 5-羟甲基糠醛, 电催化氧化, 镍基催化剂, 酸腐蚀诱导

Abstract: With the continuous improvement of solar energy production capacity, how to effectively use the electricity generated by renewable solar energy for electrochemical conversion of biomass is a hot topic. Electrochemical conversion of 5-hydroxymethylfurfural (HMF) to biofuels and value-added oxygenated commodity chemicals provides a promising and alternative pathway to convert renewable electricity into chemicals. Although nickel-based eletrocatalysts are well-known for HMF oxidation, their relatively low intrinsic activity, poor conductivity and stability still limit the potential applications. Here, we report the fabrication of a freestanding nickel-based electrode, in which Ni(OH)₂ species were in-situ constructed on Ni foam (NF) support using a facile acid-corrosion-induced strategy. The Ni(OH)₂/NF electrocatalyst exhibits stable and efficient electrochemical HMF oxidation into 2,5-furandicarboxylic acid (FDCA) with HMF conversion close to 100% with high Faraday efficiency. In-situ formation strategy results in a compact interface between Ni(OH)₂ and NF, which contributes to good conductivity and stability during electrochemical reactions. The superior performance benefits from dynamic cyclic evolution of Ni(OH)₂ to NiOOH, which acts as the reactive species for HMF oxidation to FDCA. A scaled-up device based on a continuous-flow electrolytic cell was also established, giving stable operation with a high FDCA production rate of 27 mg h^-1cm^-2. This job offers a straightforward, economical, and scalable design strategy to design efficient and durable catalysts for electrochemical conversion of valuable chemicals.

Key words: Acid-corrosion-induced, 5-Hydroxymethylfurfural, Electrocatalytic oxidation, Ni electrocatalysis

霍韵滢, 郭聪, 张永乐, 刘婧怡, 张巧, 刘芝婷, 杨光星, 李仁贵, 彭峰. 自支撑Ni(OH)₂/NF催化剂高效电催化氧化5-羟甲基糠醛反应研究[J]. 催化学报, DOI: 10.1016/S1872-2067(24)60089-6.

Yunying Huo, Cong Guo, Yongle Zhang, Jingyi Liu, Qiao Zhang, Zhiting Liu, Guangxing Yang, Rengui Li, Feng Peng. Realizing efficient electrochemical oxidation of 5-hydroxymethylfurfural on a freestanding Ni(OH)₂/nickel foam catalyst[J]. Chinese Journal of Catalysis, DOI: 10.1016/S1872-2067(24)60089-6.

×
扫码分享

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://www.cjcatal.com/CN/10.1016/S1872-2067(24)60089-6

参考文献

[1] Y. Gao, L. Ge, H. Xu, K. Davey, Y. Zheng, S.-Z. Qiao, ACS Catal., 2023, 13, 11204-11231.
[2] H. Wen, W. Zhang, Z. Fan, Z. Chen,ACS Catal., 2023, 13, 15263-15289.
[3] Y. Liu, Z. Yang, Y. Zou, S. Wang, J. He, Small, 2024, 24, 2306488.
[4] Y. Qi, B. Zhang, G. Zhang, Z. Zheng, T. Xie, S. Chen, G. Ma, C. Li, K. Domen, F. Zhang, Joule, 2024, 8, 193-203.
[5] X. Zhou, P. Wang, M. Li, M. Wu, B. Jin, J. Luo, M. Chen, X. Zhou, Y. Zhang, X. Zhou, J. Mater. Sci.Technol., 2023, 158, 171-179.
[6] S. Kunnikuruvan, N. N. Nair,ACS Catal., 2019, 9, 7250-7263.
[7] G. S. Svenningsen, R. Kumar, C. E. Wyman, P. Christopher,ACS Catal., 2018, 8, 5591-5600.
[8] C. Xu, E. Paone, D. Rodriguez-Padron, R. Luque, F. Mauriello,Chem. Soc. Rev., 2020, 49, 4273-4306.
[9] A. Gandini, T. M. Lacerda, A. J. Carvalho, E. Trovatti,Chem. Rev., 2016, 116, 1637-1669.
[10] M. Sajid, X. Zhao, D. Liu,Green Chem., 2018, 20, 5427-5453.
[11] T. Kou, M. Chen, F. Wu, T. J. Smart, S. Wang, Y. Wu, Y. Zhang, S. Li, S. Lall, Z. Zhang, Y. S. Liu, J. Guo, G. Wang, Y. Ping, Y. Li,Nat. Commun., 2020, 11, 590.
[12] Y. Li, Y. Hu, X. F. Wu,Chem. Soc. Rev., 2018, 47, 172-194.
[13] D. Formenti, F. Ferretti, F. K. Scharnagl, M. Beller,Chem. Rev., 2019, 119, 2611-2680.
[14] Y. Lu, T. Liu, Y.-C. Huang, L. Zhou, Y. Li, W. Chen, L. Yang, B. Zhou, Y. Wu, Z. Kong, Z. Huang, Y. Li, C.-L. Dong, S. Wang, Y. Zou, ACS Catal., 2022, 12, 4242-4251.
[15] Y. Lu, T. Liu, C. L. Dong, C. Yang, L. Zhou, Y. C. Huang, Y. Li, B. Zhou, Y. Zou, S. Wang,Adv. Mater., 2022, 34, 2107185.
[16] G. Grabowski, J. Lewkowski, R. Skowroński, Electrochim. Acta, 1991, 36, 1995.
[17] B. You, N. Jiang, M. Sheng, M. W. Bhushan, Y. Sun,ACS Catal., 2015, 6, 714-721.
[18] Y. Sun, C. Liu, D. C. Grauer, J. Yano, J. R. Long, P. Yang, C. J. Chang, J. Am. Chem.Soc., 2013, 135, 17699-17702.
[19] S. Barwe, J. Weidner, S. Cychy, D. M. Morales, S. Dieckhöfer, D. Hiltrop, J. Masa, M. Muhler, W. Schuhmann,Angew. Chem. Int. Ed., 2018, 57, 11460-11464.
[20] W.-J. Liu, L. Dang, Z. Xu, H.-Q. Yu, S. Jin, G. W. Huber, ACS Catal., 2018, 8, 5533-5541.
[21] N. Zhang, Y. Zou, L. Tao, W. Chen, L. Zhou, Z. Liu, B. Zhou, G. Huang, H. Lin, S. Wang,Angew. Chem. Int. Ed., 2019, 58, 15895-15903.
[22] L. Guo, X. Zhang, L. Gan, L. Pan, C. Shi, Z.-F. Huang, X. Zhang, J.-J. Zou, Adv. Sci., 2022, 10, 2205540.
[23] L. Guo, X. Zhang, L. Gan, L. Pan, C. Shi, Z. F. Huang, X. Zhang, J. J. Zou,Adv. Sci., 2022, 10, 2205551.
[24] A. Delparish, A. Uslu, Y. Cao,T. de Groot, J. van der Schaaf, T. Noël, M. Fernanda Neira d'Angelo, Chem. Eng. J., 2022, 438, 135393.
[25] Y. Wang, L. Chen, X. Yu, Y. Wang, G. Zheng,Adv. Energy Mater., 2017, 7, 1601390.
[26] S. Zhou, H. Yin, V. Schwartz, Z. Wu, D. Mullins, B. Eichhorn, S. H. Overbury, S. Dai, ChemPhysChem, 2008, 9, 2475-2479.
[27] J. Liu, B. Zhang, Y. Fo, W. Yu, J. Gao, X. Cui, X. Zhou, L. Jiang,Chem. Eng. J., 2023, 464, 142692.
[28] Y. Tan, Q. Gao, W. Tian, Y. Zhang, J. Xu,Microporous Mesoporous Mater., 2014, 200, 92-100.
[29] Y.-P. Zhu, Y.-P. Liu, T.-Z. Ren, Z.-Y. Yuan, Adv. Funct. Mater., 2015, 25, 7337-7347.
[30] Y.-H. Fang, Z.-P. Liu, ACS Catal., 2014, 4, 4364-4376.
[31] H. Fei, J. Dong, M. J.Arellano-Jimenez, G. Ye, N. Dong Kim, E. L. Samuel, Z. Peng, Z. Zhu, F. Qin, J. Bao, M. J. Yacaman, P. M. Ajayan, D. Chen, J. M. Tour, Nat. Commun., 2015, 6, 8668.
[32] L. Su, X. Cui, T. He, L. Zeng, H. Tian, Y. Song, K. Qi, B. Y. Xia,Chem. Sci., 2019, 10, 2019-2024.
[33] W. Guo, D. Li, D. Zhong, S. Chen, G. Hao, G. Liu, J. Li, Q. Zhao, Nanoscale, 2020, 12, 983-990.
[34] J. Zhang, W. Gong, H. Yin, D. Wang, Y. Zhang, H. Zhang, G. Wang, H. Zhao, ChemSusChem, 2021, 14, 2935-2942.
[35] W. Chen, L. Xu, X. Zhu, Y. C. Huang, W. Zhou, D. Wang, Y. Zhou, S. Du, Q. Li, C. Xie, L. Tao, C. L. Dong, J. Liu, Y. Wang, R. Chen, H. Su, C. Chen, Y. Zou, Y. Li, Q. Liu, S. Wang,Angew. Chem. Int. Ed., 2021, 60, 7297-7307.
[36] A. Alobaid, C. Wang, R. A. Adomaitis, J. Electrochem. Soc., 2018, 165, J3395-J3404.
[37] N. Zhang, Y. Zou, L. Tao, W. Chen, L. Zhou, Z. Liu, B. Zhou, G. Huang, H. Lin and S. Wang, Angew. Chem. Int. Ed., 2019, 131, 16042-16050.
[38] J. Huang, Y. Li, Y. Zhang, G. Rao, C. Wu, Y. Hu, X. Wang, R. Lu, Y. Li, J. Xiong,Angew. Chem. Int. Ed., 2019, 58, 17458-17464.
[39] Y. L. Lo, B. J. Hwang, Langmuir, 1998, 14, 944-950.
[40] R. Luo, Y. Li, L. Xing, N. Wang, R. Zhong, Z. Qian, C. Du, G. Yin, Y. Wang, L. Du, Appl. Catal. B, 2022, 311, 121357.
[41] W. Chen, C. Xie, Y. Wang, Y. Zou, C.-L. Dong, Y.-C. Huang, Z. Xiao, Z. Wei, S. Du, C. Chen, B. Zhou, J. Ma, S. Wang, Chem, 2020, 6, 2974-2993.
[42] W. Chen, Y. Wang, B. Wu, J. Shi, Y. Li, L. Xu, C. Xie, W. Zhou, Y.-C. Huang, T. Wang, S. Du, M. Song, D. Wang, C. Chen, J. Zheng, J. Liu, C.-L. Dong, Y. Zou, J. Chen, S. Wang, Adv. Mater., 2022, 34, 2105320.
[43] Z. Yang, B. Zhang, C. Yan, Z. Xue, T. Mu, Appl. Catal. B, 2023, 330, 122590.

自支撑Ni(OH)₂/NF催化剂高效电催化氧化5-羟甲基糠醛反应研究

Realizing efficient electrochemical oxidation of 5-hydroxymethylfurfural on a freestanding Ni(OH)₂/nickel foam catalyst

PDF

可视化

摘要/Abstract

引用本文

使用本文

扫码分享

参考文献

相关文章 15

编辑推荐

Metrics

[1]	曲虹宇, 胡文德, 李相呈, 徐睿, 韩笑, 李俊杰, 陆怡卿, 叶迎春, 王传明, 王振东, 杨为民. 具有超低镍负载的Ni-C₃N₄高效催化5-羟甲基糠醛氢解制2,5-二甲基呋喃[J]. 催化学报, 2024, 60(5): 253-261.
[2]	谷苗莉, 杨祎, 程蓓, 张留洋, 肖鹏, 陈涛. 利用电荷分离调控S型异质结光催化氧化产物选择性[J]. 催化学报, 2024, 59(4): 185-194.
[3]	齐宴宾, 朱以华, 江宏亮, 李春忠. 通过NiMo氧化物-CoMo氧化物混合物衍生催化剂中的界面相互作用促进甲醇到甲酸盐的电催化氧化[J]. 催化学报, 2024, 56(1): 139-149.
[4]	王洪芳, 徐雷涛, 吴景程, 周鹏, 陶沙沙, 逯宇轩, 吴贤文, 王双印, 邹雨芹. 通过TEMPO增强脱氢和OH吸附促进中性电解质中5-羟甲基糠醛的电催化氧化[J]. 催化学报, 2023, 46(3): 148-156.
[5]	逯宇轩, 杨柳, 姜一民, 原甑然, 王双印, 邹雨芹. 局域静电环境工程用于增强电催化生物质转化过程中羟基活性[J]. 催化学报, 2023, 53(10): 153-160.
[6]	张姜, 王子剑, 陈慕耕, 朱义峰, 刘永梅, 贺鹤勇, 曹勇, 包信和. 氮掺杂碳层包覆纳米金催化5-羟甲基糠醛非临氢转化制5-甲基糠醛[J]. 催化学报, 2022, 43(8): 2212-2222.
[7]	李振宇, 淮丽媛, 郝盼盼, 赵玺, 王永钊, 张炳森, 谌春林, 张建. 碳纳米管负载钯基催化剂催化氧化2,5-呋喃二甲醇合成2,5-呋喃二甲酸[J]. 催化学报, 2022, 43(3): 793-801.
[8]	郭斌, 贺露露, 唐钢锋, 张丽, 叶林, 岳斌, 曾适之, 贺鹤勇. 氧化钽及钽钨复合氧化物固体酸催化己糖脱水制备5-羟甲基糠醛以及非等计量比的甲酸和乙酰丙酸[J]. 催化学报, 2020, 41(8): 1248-1260.
[9]	Seyed Karim Hassaninejad-Darzi. 纳米分子筛LTA包裹Ni-Salen配合物为修饰碳糊电极用于电催化氧化肼反应[J]. 催化学报, 2018, 39(2): 283-296.
[10]	冯向东, 冯杰, 李文英. 甲烷二氧化碳重整反应中微量氧化镁助剂对Ni基催化剂抗积碳性能的影响[J]. 催化学报, 2018, 39(1): 88-98.
[11]	曹红霞, 张军, 郭成龙, 陈经广, 任相坤. 三维介孔KIT-6上高分散Ni纳米粒子用于CO甲烷化:助剂对催化性能的影响[J]. 催化学报, 2017, 38(7): 1127-1137.
[12]	申越, 康玉茹, 孙建奎, 王超, 王波, 许凤, 孙润仓. 双相体系中凹土负载型固体酸SO₄^2-/In₂O₃-ATP催化己糖降解5-羟甲基糠醛[J]. 催化学报, 2016, 37(8): 1362-1368.
[13]	Ali Benvidi, Shahriar Jahanbani, Bibi-Fatemeh Mirjalili, Reza Zare. 苯并噻唑和铁氧化物纳米粒子修饰的磁性棒碳糊电极上肼的电催化氧化反应:同时检测肼和苯酚[J]. 催化学报, 2016, 37(4): 549-560.
[14]	李伟作, 赵忠奎, 焦艳华, 王桂茹. 氧化锆担载镍甲烷干重整催化剂的载体形貌效应[J]. 催化学报, 2016, 37(12): 2122-2133.
[15]	Vladimir V. Chesnokov, Olga Yu. Podyacheva, Alexander N. Shmakov, Lidiya S. Kibis, Andrei I. Boronin, Zinfer R. Ismagilov. Ni基催化剂上未掺杂和氮掺杂的碳纳米纤维生长机理的比较[J]. 催化学报, 2016, 37(1): 169-176.