Dodecylsulfate Anion Embedded Layered Double Hydroxide Supported Nanopalladium Catalyst for the Suzuki Reaction

Chinese Journal of Catalysis ›› 2010, Vol. 31 ›› Issue (5): 557-561.

• Articles • Previous Articles Next Articles

Dodecylsulfate Anion Embedded Layered Double Hydroxide Supported Nanopalladium Catalyst for the Suzuki Reaction

LIU Shiyong1,*, ZHOU Qizhong1, JIN Zhengneng1, JIANG Huajiang1, JIANG Xuanzhen2

1School of Pharmaceutical and Chemical Engineering, Taizhou University, Linhai 317000, Zhejiang, China；2Department of Chemistry, Zhejiang University, Hangzhou 310027, Zhejiang, China

Received:2010-05-25 Online:2010-05-25 Published:2013-12-05

Abstract

Abstract: Dodecylsulfate anion embedded layered double hydroxide (LDH) supported nanopalladium catalyst was prepared. This lipophilic catalyst highly efficiently promoted the Suzuki reaction. The catalyst could be reused five times without significant loss of catalytic activity.

Key words: surfactant, layered double hydroxide, nanopalladium, mesoporous material, Suzuki reaction, aryl halide, phenylboronic acid

LIU Shiyong;*;ZHOU Qizhong;JIN Zhengneng;JIANG Huajiang;JIANG Xuanzhen. Dodecylsulfate Anion Embedded Layered Double Hydroxide Supported Nanopalladium Catalyst for the Suzuki Reaction[J]. Chinese Journal of Catalysis, 2010, 31(5): 557-561.

×
share this article

Add to citation manager EndNote|Ris|BibTeX

URL: https://www.cjcatal.com/EN/

https://www.cjcatal.com/EN/Y2010/V31/I5/557

[1]	Ping Zhang, Hao Chen, Lin Chen, Ying Xiong, Ziqi Sun, Haoyu Yang, Yingke Fu, Yaping Zhang, Ting Liao, Fei Li. Atomically dispersed Ni-N-C catalyst derived from NiZn layered double hydroxides for efficient electrochemical CO₂ reduction [J]. Chinese Journal of Catalysis, 2023, 45(2): 152-161.
[2]	Junhao Yang, Lulu An, Shuang Wang, Chenhao Zhang, Guanyu Luo, Yingquan Chen, Huiying Yang, Deli Wang. Defects engineering of layered double hydroxide-based electrocatalyst for water splitting [J]. Chinese Journal of Catalysis, 2023, 55(12): 116-136.
[3]	Qixian Xie, Dan Ren, Lichen Bai, Rile Ge, Wenhui Zhou, Lu Bai, Wei Xie, Junhu Wang, Michael Grätzel, Jingshan Luo. Investigation of nickel iron layered double hydroxide for water oxidation in different pH electrolytes [J]. Chinese Journal of Catalysis, 2023, 44(1): 127-138.
[4]	Xue Bai, Zhiyao Duan, Bing Nan, Liming Wang, Tianmi Tang, Jingqi Guan. Unveiling the active sites of ultrathin Co-Fe layered double hydroxides for the oxygen evolution reaction [J]. Chinese Journal of Catalysis, 2022, 43(8): 2240-2248.
[5]	Jinling Cheng, Dingsheng Wang. 2D materials modulating layered double hydroxides for electrocatalytic water splitting [J]. Chinese Journal of Catalysis, 2022, 43(6): 1380-1398.
[6]	Gen Huang, Yingying Li, Ru Chen, Zhaohui Xiao, Shiqian Du, Yucheng Huang, Chao Xie, Chungli Dong, Haibo Yi, Shuangyin Wang. Electrochemically formed PtFeNi alloy nanoparticles on defective NiFe LDHs with charge transfer for efficient water splitting [J]. Chinese Journal of Catalysis, 2022, 43(4): 1101-1110.
[7]	Kailin Wang, Tianqi Wang, Quazi Arif Islam, Yan Wu. Layered double hydroxide photocatalysts for solar fuel production [J]. Chinese Journal of Catalysis, 2021, 42(11): 1944-1975.
[8]	Shenzhou Li, Jianyun Liu, Shuo Duan, Tanyuan Wang, Qing Li. Tuning the oxygen evolution electrocatalysis on NiFe-layered double hydroxides via sulfur doping [J]. Chinese Journal of Catalysis, 2020, 41(5): 847-852.
[9]	Shuangde Li, Dongdong Wang, Xiaofeng Wu, Yunfa Chen. Recent advance on VOCs oxidation over layered double hydroxides derived mixed metal oxides [J]. Chinese Journal of Catalysis, 2020, 41(4): 550-560.
[10]	Ruowen Liang, Zhiyu Liang, Feng Chen, Danhua Xie, Yanling Wu, Xuxu Wang, Guiyang Yan, Ling Wu. Sodium dodecyl sulfate-decorated MOF-derived porous Fe₂O₃ nanoparticles: High performance, recyclable photocatalysts for fuel denitrification [J]. Chinese Journal of Catalysis, 2020, 41(1): 188-199.
[11]	Jiahua Zhao, Yuan Shu, Pengfei Zhang. Solid-state CTAB-assisted synthesis of mesoporous Fe₃O₄ and Au@Fe₃O₄ by mechanochemistry [J]. Chinese Journal of Catalysis, 2019, 40(7): 1078-1084.
[12]	Liangliang Huang, Yuqin Zou, Dawei Chen, Shuangyin Wang. Electronic structure regulation on layered double hydroxides for oxygen evolution reaction [J]. Chinese Journal of Catalysis, 2019, 40(12): 1822-1840.
[13]	Ekaterina Kholkina, Paivi Maki-Arvela, Chloe Lozachmeuer, Roman Barakov, Nataliya Shcherban, Dmitry Yu. Murzin. Prins cyclisation of (-)-isopulegol with benzaldehyde over ZSM-5 based micro-mesoporous catalysts for production of pharmaceuticals [J]. Chinese Journal of Catalysis, 2019, 40(11): 1713-1720.
[14]	Weiwei Lin, Haiyang Cheng, Xiaoru Li, Chao Zhang, FengyuZhao, Masahiko Arai. Layered double hydroxide-like Mg₃Al_1-xFe_x materials as supports for Ir catalysts:Promotional effects of Fe doping in selective hydrogenation of cinnamaldehyde [J]. Chinese Journal of Catalysis, 2018, 39(5): 988-996.
[15]	Zhaoxiong Yan, Zhihua Xu, Lin Yue, Ling Shi, Linyong Huang. Hierarchical Ni-Al hydrotalcite supported Pt catalyst for efficient catalytic oxidation of formaldehyde at room temperature [J]. Chinese Journal of Catalysis, 2018, 39(12): 1919-1928.

Dodecylsulfate Anion Embedded Layered Double Hydroxide Supported Nanopalladium Catalyst for the Suzuki Reaction

PDF (PC)

Knowledge

Cited

Abstract

Cite this article

share this article

share this article

References

Related Articles 15

Recommended Articles

Metrics