Catalytic oxidation of styrene to benzaldehyde over a copper Schiff-base/SBA-15 catalyst

doi:10.1016/S1872-2067(14)60131-5

Abstract

Abstract:

The amino-modified mesoporous material SBA-15 (NH₂-SBA-15) was prepared via co-condensation of tetraethylorthosilicate with 3-aminopropyltriethoxysilane in the presence of an amphiphilic triblock copolymer as a pore-directing agent under acidic conditions. The SBA-15-supported Cu Schiff-base complex (Cu-SBA-15) was then synthesized by condensation of salicylaldehyde with NH₂-SBA-15, followed by the addition of a solution of Cu(NO₃)₂. The supported complex was systematically characterized by elemental analysis, inductive coupled high frequency plasma atomic emission spectrometry, powder X-ray diffraction, Fourier transform infrared spectroscopy, ultraviolet-visible spectroscopy, field scanning electron microscopy, transmission electron microscopy, N₂ absorption-desorption, and thermo gravimetric analysis, and was used as the catalyst for the selective oxidation of styrene to benzaldehyde. The influence of the reaction parameters was assessed. The maximum conversion of styrene was 84.4% and the selectivity for benzaldehyde was 83.9%, when the reaction was conducted with a 2:1 molar ratio of H₂O₂:styrene in the presence of 3.8 wt% catalyst at 100 ℃ for 8 h. The TOF was 261.1 h^-1, and the catalyst could be used three times without significant loss of activity. The uniformly sized pore channels, high specific surface area, and well-distributed active centers of the catalyst may contribute to the high activity.

Key words: Copper(II) Schiff base, SBA-15, Styrene oxidation, Benzaldehyde, Heterogeneous catalysis

Xuecheng Zhu, Ruwei Shen, Lixiong Zhang. Catalytic oxidation of styrene to benzaldehyde over a copper Schiff-base/SBA-15 catalyst[J]. Chinese Journal of Catalysis, 2014, 35(10): 1716-1726.

×
share this article

Add to citation manager EndNote|Ris|BibTeX

URL: https://www.cjcatal.com/EN/10.1016/S1872-2067(14)60131-5

https://www.cjcatal.com/EN/Y2014/V35/I10/1716

References

[1] Kirk-Othmer. Encyclopedia of Chemical Technology. 5th ED. John Wiley & Sons, Inc. 2007, 3: 590
[2] Wang Y, Qiao X. Fin Chem Interm (王毅, 乔旭. 精细化工中间体), 2005, 35: 44
[3] Tang S W. [PhD Dissertation]. Chengdu: Sichuan University (唐盛伟. [博士学位论文]. 成都: 四川大学), 2005
[4] Zhang X, Zhang L X, Xu N P. Petochem Technol (张旭, 张利雄, 徐南平. 石油化工), 2009, 38: 215
[5] Chen D D, Li N K, Sun P, Kong Y. Chin J Catal (陈丹丹, 李年凯, 孙鹏, 孔岩. 催化学报), 2009, 30: 643
[6] Shi F, Tse M K, Pohl M M, Brückner A, Zhang S M, Beller M. Angew Chem Int Ed, 2007, 46: 8866
[7] Lu X H, Lei J, Zhou D, Fang S Y, Dong Y L, Xia Q H. Indian J Chem A, 2010, 49: 1586
[8] Adam F, Iqbal A. Microporous Mesoporous Mater, 2011, 141: 119
[9] Pardeshi S K, Pawar R Y. J Mol Catal A, 2011, 334: 35
[10] Rajabi F, Karimi N, Saidi M R, Primo A, Varma R S, Luque R. Adv Synth Catal, 2012, 354: 1707
[11] Zhou L, Madix R J. Surf Sci, 2009, 603: 1751
[12] Polshettiwar V, Varma R S. Org Biomol Chem, 2009, 7: 37
[13] Zhang X, Zeng C F, Zhang L X, Xu N P. Kinet Catal, 2009, 50: 199
[14] Xiao Z W, He H Y. Chin J Catal (肖质文, 何红运. 催化学报), 2010, 31: 705
[15] Hu J L, Li K X, Li W, Ma F Y, Guo Y H. Appl Catal A, 2009, 364: 211
[16] Patel A, Pathan S. Ind Eng Chem Res, 2012, 51: 732
[17] Qiu M, Liu G S, Yao X Q, Guo M Y, Pan G Z, Zheng Z. Chin J Catal (仇敏, 刘国生, 姚小泉, 郭明彦, 潘桂芝, 郑卓. 催化学报), 2001, 22: 78
[18] Pasc-Banu A, Sugisaki C, Gharsa T, Marty J D, Gascon I, Krämer M, Pozzi G, Desbat B, Quici S, Rico-Lattes I, Mingotaud C. Chem Eur J, 2005, 11: 6032
[19] Silva M, Freire C, de Castro B, Figueiredo J L. J Mol Catal A, 2006, 258: 327
[20] Ku?niarska-Biernacka I, Rodrigues B, Carvalho M A, Neves I C, Fonseca A M. Appl Organomet Chem, 2012, 26: 44
[21] Maurya M R, Saini P, Kumar A, Costa Pessoa J. Eur J Inorg Chem, 2011, 31: 4846
[22] Ku?niarska-Biernacka I, Fonseca A M, Neves I C. Inorg Chim Acta, 2013, 394: 591
[23] Jana S, Dutta B, Bera R, Koner S. Langmuir, 2007, 23: 2492
[24] Yang Y, Guan J Q, Qiu P P, Kan Q B. Appl Surf Sci, 2010, 256: 3346
[25] Yang Y, Zhang Y, Hao S J, Guan J Q, Ding H, Shang F P, Qiu P P, Kan Q B. Appl Catal A, 2010, 381: 274
[26] Anand N, Reddy K H P, Swapna V, Rao K S R, Burri D R. Microporous Mesoporous Mater, 2011, 143: 132
[27] Anand N, Reddy K H P, Rao K S R, Burri D R. Catal Lett, 2011, 141: 1355
[28] Yang Y, Zhang Y, Hao S J, Kan Q B. Chem Eng J, 2011, 171: 1356
[29] Islam S M, Mondal P, Mukherjee S, Roy A S, Bhaumik A. Polym Adv Technol, 2011, 22: 933
[30] Tamami B, Ghasemi S. Appl Catal A, 2011, 393: 242
[31] Dai X, Gao B J, Lei H B. Chin J Catal (代新, 高保娇, 雷海波. 催化学报), 2012, 33: 885
[32] Sripathi V G P, Mojet B L, Nijmeijer A, Benes N E. Microporous Mesoporous Mater, 2013, 172: 1
[33] Lim M H, Stein A. Chem Mater, 1999, 11: 3285
[34] Macquarrie D J, Jackson D B. Chem Commun, 1997, 18: 1781
[35] Wang X G, Chan J C C, Tseng Y H, Cheng S F. Microporous Mesoporous Mater, 2006, 95: 57
[36] Wang X G, Lin K S K, Chan J C C, Cheng S F. J Phys Chem B, 2005, 109: 1763