碳纳米管封装铁纳米粒子催化剂上CO加氢制低碳烯烃

doi:10.1016/S1872-2067(15)60882-8

催化学报 ›› 2015, Vol. 36 ›› Issue (9): 1631-1637.DOI: 10.1016/S1872-2067(15)60882-8

碳纳米管封装铁纳米粒子催化剂上CO加氢制低碳烯烃

陈晓琪, 邓德会, 潘秀莲, 包信和

中国科学院大连化学物理研究所, 能源材料化学协同创新中心, 催化基础国家重点实验室, 辽宁大连116023

收稿日期:2015-03-30 修回日期:2015-05-05 出版日期:2015-08-28 发布日期:2015-09-26
通讯作者: 邓德会, 电话: (0411)84686637; 传真: (0411)84379128; 电子信箱: dhdeng@dicp.ac.cn; 包信和, 电话: (0411)84686637; 传真: (0411)84379128; 电子信箱: xhbao@dicp.ac.cn
基金资助:
国家自然科学基金(21321002, 21303191); 中国科学院战略性先导科技专项(A类)资助(XDA09030100).

Iron catalyst encapsulated in carbon nanotubes for CO hydrogenation to light olefins

Xiaoqi Chen, Dehui Deng, Xiulian Pan, Xinhe Bao

State Key Laboratory of Catalysis, Collaborative Innovation Center of Chemistry for Energy Materials, Dalian Institute of Chemical Physics, Chinese Academy of Sciences, Dalian 116023, Liaoning, China

Received:2015-03-30 Revised:2015-05-05 Online:2015-08-28 Published:2015-09-26
Supported by:
This work was supported by the National Natural Science Foundation of China (21321002 and 21303191) and the Strategic Priority Research Program of the Chinese Academy of Sciences (XDA09030100).

摘要/Abstract

摘要：

由于石油资源的逐步枯竭, 近年来费托(F-T)反应因其可以高效将煤、天然气和生物质等转化成液体燃料和高值化学品而越来越受到人们的关注. 相比于Co, Ni和Ru等F-T催化剂, Fe基催化剂因其价格低廉, 产物分布广而被广泛研究. 以合成气直接制备低碳烯烃的F-T过程为例, 铁基催化剂通常会因积碳和烧结的问题, 而导致失活. 因此, 人们通常使用一些氧化物载体, 比如氧化硅, 氧化铝或者分子筛来分散并稳定铁粒子. 但是这类氧化物载体通常与铁有非常强的相互作用, 特别是在铁粒子较小的情况下, 容易生成一些难于还原的硅酸铁和铝酸铁. 而活性炭、碳纤维等惰性载体与铁的相互作用较弱, 不足以稳定小的铁粒子在而反应过程中聚集. 近来, 我们组提出了利用石墨烯碳层封装过渡金属粒子作为催化剂, 利用"穿透"的金属电子来催化反应, 从而可以使活性中心和反应介质隔离, 有效地增强了非贵金属催化剂的活性和稳定性. 在此基础上, 我们组和其他课题组的研究表明, 一系列石墨烯碳层封装的非贵金属催化剂在燃料电池阴极氧还原反应, 电催化析氢反应, 染料敏化太阳能电池中的I₃^-还原反应以及催化氧化还原反应中都有着广泛的应用前景. 这种材料中碳层不仅能在氧化气氛、酸性介质中保护包覆的金属, 防止其被氧化或者腐蚀, 还与包覆的金属有着较强的相互作用, 可以促进非贵金属的电子向碳层表面的转移, 有望在一些苛刻的反应条件下实现对贵金属催化剂的替代. 本文进一步拓展了其在高温反应中的应用, 发现豆荚状碳纳米管封装的金属铁纳米粒子在合成气制备低碳烯烃中可以有效防止金属铁纳米粒子的烧结和聚集, 因此表现出优异的低碳烯烃选择性和催化稳定性.
我们利用一步化学反应法合成了豆荚状碳纳米管封装的铁纳米粒子催化剂(Pod-Fe), 并通过酸洗除去碳管外面裸露的铁粒子. 透射电镜(TEM)和X射线衍射(XRD)表明酸洗后铁粒子被包覆在碳管内, 并且呈金属态, 而酸洗前, 则还有大量的氧化铁粒子分布于碳管外部(FeO_x/Pod-Fe). 将酸洗前后的两个催化剂用于固定床气相F-T反应中. 通过调节空速和温度考察了它们的催化反应性能, 结果表明两个催化剂在不同的反应条件下都有着良好的低碳烯烃选择性. 不同反应温度下, 它们表现出不同的变化趋势: Pod-Fe活性随着温度的升高而缓慢增长, 至380℃都没有明显的失活现象; 而对于FeO_x/Pod-Fe催化剂, 随着温度的升高, CO的转化率先升高, 在300℃时达最高, 但随着温度进一步升高, 活性迅速降低, 呈现一个火山型曲线. TEM结果发现, 反应后FeO_x/Pod-Fe催化剂粒子上产生了很多杂乱的碳丝, 并且铁粒子有着明显的聚集长大. 而Pod-Fe催化剂即使在380℃反应后, 其形貌仍然保持完好, 没有积碳产生, 粒子也没有发生聚集和长大. 进一步在320℃下120 h的寿命试验发现, Pod-Fe催化剂的初始活性较低, 但经20 h的活化阶段, 活性会先增加后略有下降, 20 h后趋于稳定. 而FeO_x/Pod-Fe催化剂在反应初始虽然表现出较高的活性, 但是随着时间进行, 活性迅速下降一半以上, 最后趋于稳定. 同时结合反应后TEM和XRD的结果发现碳管外部裸露的铁粒子会在反应过程中形成碳化铁物种, 并随着反应进行产生聚集, 并伴有大量积碳, 导致活性迅速下降; 而碳层的包覆对于铁粒子有着很好的稳定作用, 使得铁粒子能够在高温反应中保持稳定, 并且没有积碳的产生. 由此可见石墨烯碳层可以有效保护其包覆的金属粒子, 并且能够提高其在高温反应下的低碳烯烃选择性和稳定性. 此类催化剂有望在一些苛刻条件下的多相催化反应中得到广泛应用.

关键词: 费托合成, 稳定性, 低碳烯烃, 碳纳米管, 铁纳米粒子

Abstract:

Fe-based catalyst is an outstanding candidate for the Fischer-Tropsch reaction to get light olefins from syngas directly. However, exposed Fe species are susceptible to sintering and coking, which lead to deactivation. Here, we demonstrate that Fe nanoparticles encapsulated in pod-like carbon nanotubes (Pod-Fe) can be used as an efficient Fischer-Tropsch catalyst to produce light olefins. It gave a higher selectivity of light olefins (45%) and high stability over 120 h reaction (P=0.5 MPa, T=320℃, CO:H₂= 1:2, gas hourly space velocity=3500 h^-1). A catalyst with exposed Fe particles on the outside of the Pod-Fe (FeO_x/Pod-Fe) catalyst showed a selectivity of light olefins of 42%, but had a significantly lower stability due to the agglomeration of Fe nanoparticles and carbon deposition. These results indicated that the graphene shell of Pod-Fe played an important role in protecting the Fe particles and provided a rational way to enhance the activity and stability of Fe-based catalysts in high temperature reactions.

Key words: Fischer-Tropsch synthesis, Stability, Light olefins, Carbon nanotubes, Iron nanoparticles

陈晓琪, 邓德会, 潘秀莲, 包信和. 碳纳米管封装铁纳米粒子催化剂上CO加氢制低碳烯烃[J]. 催化学报, 2015, 36(9): 1631-1637.

Xiaoqi Chen, Dehui Deng, Xiulian Pan, Xinhe Bao. Iron catalyst encapsulated in carbon nanotubes for CO hydrogenation to light olefins[J]. Chinese Journal of Catalysis, 2015, 36(9): 1631-1637.

×
扫码分享

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://www.cjcatal.com/CN/10.1016/S1872-2067(15)60882-8

https://www.cjcatal.com/CN/Y2015/V36/I9/1631

参考文献

[1] Schulz H. Appl Catal A, 1999, 186: 3
[2] Tijmensen M J A, Faaij A P C, Hamelinck C N, van Hardeveld M R M. Biomass Bioenergy, 2002, 23: 129
[3] Torres Galvis H M, Bitter J H, Khare C B, Ruitenbeek M, Dugulan A I, de Jong K P. Science, 2012, 335: 835
[4] Torres Galvis H M, de Jong K P. ACS Catal, 2013, 3: 2130
[5] Khodakov A Y, Chu W, Fongarland P. Chem Rev, 2007, 107: 1692
[6] Davis B H. Ind Eng Chem Res, 2007, 46: 8938
[7] Van Der Laan G P, Beenackers A A C M. Catal Rev-Sci Eng, 1999, 41: 255
[8] Iglesia E, Soled S L, Fiato R A. J Catal, 1992, 137: 212
[9] Li S Z, Li A W, Krishnamoorthy S, Iglesia E. Catal Lett, 2001, 77: 197
[10] Zhang Q H, Kang J C, Wang Y. ChemCatChem, 2010, 2: 1030
[11] Yang Z Q, Guo S J, Pan X L, Wang J H, Bao X H. Energy Environ Sci, 2011, 4: 4500
[12] Janardanarao M. Ind Eng Chem Res, 1990, 29: 1735
[13] Chen W, Fan Z L, Pan X L, Bao X H. J Am Chem Soc, 2008, 130: 9414
[14] de Smit E, Weckhuysen B M. Chem Soc Rev, 2008, 37: 2758
[15] Koeken A C J, Torres Galvis H M, Davidian T, Ruitenbeek M, de Jong K P. Angew Chem Int Ed, 2012, 51: 7190
[16] Niemantsverdriet J W, Van der Kraan A M, Van Dijk W L, Van der Baan H S. J Phys Chem, 1980, 84: 3363
[17] Wan H J, Wu B S, Zhang C H, Xiang H W, Li Y W, Xu B F, Yi F. Catal Commun, 2007, 8: 1538
[18] Zhang C H, Yang Y, Teng B T, Li T Z, Zheng H Y, Xiang H W, Li Y W. J Catal, 2006, 237: 405
[19] Pour A N, Zamani Y, Tavasoli A, Kamali Shahri S M, Taheri S A. Fuel, 2008, 87: 2004
[20] Pour A N, Shahri S M K, Zamani Y, Irani M, Tehrani S. J Nat Gas Chem, 2008, 17: 242
[21] Perrichon V, Charcosset H, Barrault J, Forquy C. Appl Catal, 1983, 7: 21
[22] Raupp G B, Delgass W N. J Catal, 1979, 58: 337
[23] Zhang C H, Wan H J, Yang Y, Xiang H W, Li Y W. Catal Commun, 2006, 7: 733
[24] Deng D H, Yu L, Chen X Q, Wang G X, Jin L, Pan X L, Deng J, Sun G Q, Bao X H. Angew Chem Int Ed, 2013, 52: 371
[25] Deng J, Yu L, Deng D H, Chen X Q, Yang F, Bao X H. J Mater Chem A, 2013, 1: 14868
[26] Deng J, Ren P J, Deng D H, Yu L, Yang F, Bao X H. Energy Environ Sci, 2014, 7: 1919
[27] Deng J, Ren P J, Deng D H, Bao X H. Angew Chem Int Ed, 2015, 54: 2100
[28] Chen X Q, Xiao J P, Wang J, Deng D H, Hu Y F, Zhou J G, Yu L, Heine T, Pan X L, Bao X H. Chem Sci, 2015, 6: 3262
[29] Wang J, Wang G X, Miao S, Jiang X L, Li J Y, Bao X H. Carbon, 2014, 75: 381
[30] Hu Y, Jensen J O, Zhang W, Cleemann L N, Xing W, Bjerrum N J, Li Q F. Angew Chem, Int Ed, 2014, 53: 3675
[31] Zheng X J, Deng J, Wang N, Deng D H, Zhang W H, Bao X H, Li C. Angew Chem, Int Ed, 2014, 53: 7023
[32] Fu T, Wang M, Cai W M, Cui Y M, Gao F, Peng L M, Chen W, Ding W P. ACS Catal, 2014, 4: 2536
[33] Luo J, Yu H, Wang H J, Peng F. Catal Commun, 2014, 51: 77
[34] Keiski R L, Salmi T, Niemistö P, Ainassaari J, Pohjola V J. Appl Catal A, 1996, 137: 349
[35] Rhodes C, Peter Williams B, King F, Hutchings G J. Catal Commun, 2002, 3: 381
[36] Edwards M A, Whittle D M, Rhodes C, Ward A M, Rohan D, Shannon M D, Hutchings G J, Kiely C J. Phys Chem Chem Phys, 2002, 4: 3902
[37] Yang C, Zhao H B, Hou Y L, Ma D. J Am Chem Soc, 2012, 134: 15814
[38] de Smit E, Beale A M, Nikitenko S, Weckhuysen B M. J Catal, 2009, 262: 244

碳纳米管封装铁纳米粒子催化剂上CO加氢制低碳烯烃

Iron catalyst encapsulated in carbon nanotubes for CO hydrogenation to light olefins

PDF

可视化

被引次数

摘要/Abstract

引用本文

使用本文

扫码分享

参考文献

相关文章 15

编辑推荐

Metrics

[1]	安国庆, 张晓伟, 张灿阳, 高鸿毅, 刘斯奇, 秦耕, 齐辉, Jitti Kasemchainan, 张建伟, 王戈. 金属有机骨架基绿色催化剂在醇氧化反应中的研究应用[J]. 催化学报, 2023, 50(7): 126-174.
[2]	刘培功, 林铁军, 郭磊, 刘晓哲, 龚坤, 尧泰真, 安芸蕾, 钟良枢. 调控Co₂C局域浸润环境实现高碳效合成气直接制烯烃[J]. 催化学报, 2023, 48(5): 150-163.
[3]	董兴宗, 刘广业, 陈兆安, 张权, 徐云鹏, 刘中民. 性能优异的Pd-[DBU][Cl]/AC无汞催化剂在乙炔氢氯化中的应用[J]. 催化学报, 2023, 46(3): 137-147.
[4]	Diab khalafallah, 张运祥, 王昊, Jong-Min Lee, 张勤芳. 联产混合电解水策略实现节能电化学制氢的最新进展[J]. 催化学报, 2023, 55(12): 44-115.
[5]	吴立清, 梁庆, 赵家仪, 朱娟, 贾宏男, 张伟, 蔡苹, 罗威. 铋掺杂的二氧化钌催化剂用于高效酸性水氧化[J]. 催化学报, 2023, 55(12): 182-190.
[6]	李航杰, 肖月华, 肖佳乐, 范凯, 李炳宽, 李晓龙, 王亮, 肖丰收. 镓改性的铜基疏水催化剂用于CO₂选择性加氢制二甲醚的研究[J]. 催化学报, 2023, 54(11): 178-187.
[7]	夏苏为, 周其兴, 孙若栩, 陈立章, 张明义, 庞欢, 徐林, 杨军, 唐亚文. 在N掺杂碳纳米管/纳米线耦合超结构中原位固载CoNi纳米颗粒制备莫特-肖特基催化剂并用于高效电催化氧还原反应[J]. 催化学报, 2023, 54(11): 278-289.
[8]	付先彪. 关于电还原硝酸根反应的思考[J]. 催化学报, 2023, 53(10): 8-12.
[9]	乔玉彦, 潘艳秋, 张江威, 王彬, 武婷婷, 范文俊, 曹雨程, Rashid Mehmood, 张飞, 章福祥. 多碳界面工程用于促进NiFe纳米复合电催化剂的产氧反应[J]. 催化学报, 2022, 43(9): 2354-2362.
[10]	张琪, 陈辉, 杨岚, 梁宵, 石磊, 冯庆, 邹永存, 李国栋, 邹晓新. 非催化瞬态铱脱溶—筛选铱基钙钛矿析氧催化剂时不可忽视的实验现象[J]. 催化学报, 2022, 43(3): 885-893.
[11]	孟祥东, 甄超, 刘岗, 成会明. Cu₃N保护壳层稳定CuO光阴极[J]. 催化学报, 2022, 43(3): 755-760.
[12]	刘军辉, 宋亚坤, 郭旭明, 宋春山, 郭新闻. 铁基催化剂在CO_x加氢制高附加值烃反应中的应用[J]. 催化学报, 2022, 43(3): 731-754.
[13]	冯业芹, 秦琳, 张峻豪, 符方玉, 李慧杰, 相华, 吕红金. 轮型二十核铜取代多金属氧酸盐催化剂: 光催化制氢的机理和稳定性研究[J]. 催化学报, 2022, 43(2): 442-450.
[14]	王同宝, 韩光泰, 王子运, 王昱沆. 克服高温二氧化碳电解产生的碳沉积问题[J]. 催化学报, 2022, 43(12): 2938-2945.
[15]	吕宏伟, 国文馨, 陈敏, 周煌, 吴宇恩. 热稳定单原子催化剂的理性构筑: 从原子级结构到实际应用[J]. 催化学报, 2022, 43(1): 71-91.