Pd/PbTiO3表面的热电效应增强光催化Suzuki偶联反应

doi:10.1016/S1872-2067(20)63581-1

催化学报 ›› 2020, Vol. 41 ›› Issue (10): 1674-1681.DOI: 10.1016/S1872-2067(20)63581-1

• 论文 • 上一篇

Pd/PbTiO₃表面的热电效应增强光催化Suzuki偶联反应

闻洁雅^a, 凌丽丽^b, 陈瑶^a, 卞振锋^a

a 上海师范大学, 资源化学教育部重点实验室, 稀土功能材料上海重点实验室, 上海 200234;
b 上海电力大学, 上海 201303

收稿日期:2020-02-21 修回日期:2020-03-25 出版日期:2020-10-18 发布日期:2020-08-15
通讯作者: 卞振锋
基金资助:
国家自然科学基金（21876114，217611142011，51572174）和上海市科委（19160712900），资源化学国际合作联合实验室（IJLRC），教育部（PCSIRT_IRT_16R49）.上海市特聘教授（东方学者）和上海市曙光学者.上海绿色能源化工工程研究中心（18DZ2254200）.

Pyroelectricity effect on photoactivating palladium nanoparticles in PbTiO₃ for Suzuki coupling reaction

Jieya Wen^a, Lili Ling^b, Yao Chen^a, Zhenfeng Bian^a

a The Education Ministry Key Laboratory of Resource Chemistry and Shanghai Key Laboratory of Rare Earth Functional Materials, Shanghai Normal University, Shanghai 200234, China;
b Shanghai University of Electric Power, Shanghai 201303, China

Received:2020-02-21 Revised:2020-03-25 Online:2020-10-18 Published:2020-08-15
Supported by:
This work was supported by the National Natural Science Foundation of China (21876114, 21761142011, 51572174), Shanghai Government (19160712900), International Joint Laboratory on Resource Chemistry (IJLRC), and Ministry of Education of China (PCSIRT_IRT_16R49). Research is also supported by The Program for Professor of Special Appointment (Eastern Scholar) at Shanghai Institutions of Higher Learning and Shuguang Research Program of Shanghai Education Committee. Shanghai Engineering Research Center of Green Energy Chemical Engineering (18DZ2254200).

摘要/Abstract

摘要： 发展绿色化学技术是21世纪化学研究的一个重要方向，其主要目标是取代那些对环境有害的耗能过程，其中新能源尤其是太阳能开发利用的重要性愈加突显.光催化作为一种低能耗、高效、无二次污染的技术，以其反应条件温和、能直接利用太阳能转化为化学能的优势而备受科研人员关注.光催化技术是利用半导体材料作为催化剂的光催化过程，当能量高于半导体禁带宽度的光子照射半导体材料时，半导体材料上的价带电子发生带间跃迁，从价带跃迁到导带，从而产生带正电荷的光致空穴和带负电荷的光生电子.光致空穴的强氧化能力和光生电子的还原能力导致半导体光催化剂引发一系列光催化反应的发生.光催化选择性氧化还原体系的出现和应用极大地满足了人们对能源和环境的要求.在光催化选择性氧化还原体系中，反应发生所需要的条件比传统催化温和，同时它也避免了一些危险的强氧化剂和还原性物质的使用.但是在一些过程中，催化反应常常需要在高温下进行.传统加热是由外部热源通过热辐射由表及里的热传导的方式进行的，并且为了达到催化温度，需使催化剂床层整体升温.而微波诱导的催化方法与常规不同，微波不仅加热速度快、能源利用率高，而且加热均匀、温度梯度小，因此微波化学作为一门新兴的前沿交叉学科，已在广泛的实际应用中显示出强大的生命力.将光催化技术与微波联用可能会取得意想不到的成果.
微波与光催化系统相结合是抑制光生电子-空穴复合并增强光催化反应性能的一种有效方法.本文通过简单的水热反应制备了单晶PbTiO₃纳米片.由XRD谱可以看出，所有衍射峰均归属于四方钙钛矿相PbTiO₃，紫外-可见漫反射光谱表明单晶PbTiO₃在紫外光区域有强吸收，在400-450nm处还存在微弱的可见光吸收.另外，负载了Pd纳米颗粒之后，在可见光区域吸收明显增强.这说明我们成功制备了一种既能利用微波又能利用光催化的Pd/PbTiO₃催化剂.利用PbTiO₃晶体的热释电效应在微波场下与紫外光协同促进以溴苯引导的Suzuki偶联反应发生，反应速度和选择性显著提高.在微波场和紫外光的协同作用下，PbTiO₃晶体的热电效应可以将热能转换为电能，产生正电荷和负电荷（q⁺和q^-），而Pd纳米粒子则显著提高了光催化过程的量子效率.光催化技术协同微波场可以直接作用于有机化学反应，以独特的方式促进甚至改变各种化学反应过程.

关键词: 光催化, 热释电, 微波, Suzuki偶联反应

Abstract: Combining microwave radiation with photocatalytic systems is a promising method to inhibit photogenerated electron-hole recombination and enhance the photocatalytic reaction performance. In this study, we have designed Pd/PbTiO₃ catalysts that can use both microwave fields and photocatalysis. Benefiting from the synergistic effect of microwave field and UV light, the PbTiO₃ crystals convert thermal energy into electrical energy via the pyroelectricity effect, generating positive and negative charges (q⁺ and q^-), while Pd nanoparticles significantly improve the quantum efficiency of the photocatalytic process. The composite catalyst significantly enhances the reaction rate and selectivity of the model Suzuki coupling reaction performed with bromobenzene. Microwave fields can directly act on chemical systems, promoting or changing various chemical reactions in unique ways.

Key words: Photocatalysis, Pyroelectricity, Microwave, Suzuki coupling reaction

闻洁雅, 凌丽丽, 陈瑶, 卞振锋. Pd/PbTiO₃表面的热电效应增强光催化Suzuki偶联反应[J]. 催化学报, 2020, 41(10): 1674-1681.

Jieya Wen, Lili Ling, Yao Chen, Zhenfeng Bian. Pyroelectricity effect on photoactivating palladium nanoparticles in PbTiO₃ for Suzuki coupling reaction[J]. Chinese Journal of Catalysis, 2020, 41(10): 1674-1681.

×
扫码分享

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://www.cjcatal.com/CN/10.1016/S1872-2067(20)63581-1

https://www.cjcatal.com/CN/Y2020/V41/I10/1674

参考文献

[1] E. Menachem, W. A. Phillip, Science, 2011, 333, 712-717.
[2] J. Fu, Y. L. Tian, B. B. Chang, F. N. Xi, J. Mater. Chem., 2012, 22, 21159-21166.
[3] Y. Chen, X. M. Deng, J. Y. Wen, J. Zhu, Z. F. Bian, Appl. Catal. B, 2019, 258, 118024.
[4] L. L. Ling, L. F. Liu, Y. W. Feng, J. Zhu, Z. F. Bian, Chin. J. Catal., 2018, 39, 639-645.
[5] G. Palmisano, V. Augugliaro, M. Pagliaro, L. Palmisano, Chem. Commun., 2007, 33, 3425-3437.
[6] X. M. Deng, Y. Chen, J. Y. Wen, Y. Xu, J. Zhu, Z. F. Bian, Sci. Bull., 2020, 65, 105-112.
[7] A. Fujishima, T. N. Rao, D. A. Tryk, J. Photochem. Photobiol. C, 2000, 1, 1-21.
[8] N. Hoffmann, ChemSusChem, 2012, 5, 352-371.
[9] Y. X. Zhang, M. J. Xu, H. X. Li, H. Ge, Z. F. Bian, Appl. Catal. B, 2018, 226, 213-219.
[10] M. J. Xu, Y. Chen, J. T. Qin, Y. W. Feng, W. Li, W. Chen, J. Zhu, H. X. Li, Z. F. Bian, Environ. Sci. Technol., 2018, 52, 13879-13886.
[11] H. Frank, T. Andreas, S. Frank, M. T. Reetz, Angew. Chem. Int. Ed., 2010, 46, 2903-2906.
[12] H. Shimizu, S. Onitsuka, H. Egami, T. Katsuki, J. Am. Chem. Soc., 2005, 127, 5396-5413.
[13] A. Dhakshinamoorthy, H. Garcia, Chem. Soc. Rev., 2014, 43, 5750-5765.
[14] Z. M. Xu, R. Zheng, Y. Chen, J. Zhu, Z. F. Bian, Chin. J. Catal., 2019, 40, 631-637.
[15] N. Hoffmann, Aust. J. Chem., 2015, 68, 1621-1639.
[16] Z. Wu, F. Xiong, Z. Wang, W. Huang, Chin. Chem. Lett., 2018, 29, 752-756.
[17] Y. Feng, H. Li, Ling, S. Yan, D. L. Pan, H. Ge, H. X. Li, Z. F. Bian, Environ. Sci. Technol., 2018, 52, 7842-7848.
[18] Y. W. Feng, L. L. Ling, J. Nie, K. Han, X. Chen, Z. F. Bian, H. X. Li, Z. L. Wang, ACS Nano, 2017, 11, 12411-12418.
[19] L. L. Ling, Y. W. Feng, H. Li, Y. Chen, J. Y. Wen, J. Zhu, Z. F. Bian, Appl. Surf. Sci., 2019, 483, 772-778.
[20] W. Zhang, X. Wang, X. Fu, Chem. Commun., 2003, 9, 2196-2197.
[21] S. Horikoshi, H. Tsutsumi, H. Matsuzaki, A. Furube, A. V. Emeline, N. Serpone, J. Mater. Chem. C, 2015, 3, 5958-5969.
[22] D. Z. Li, Acta Phys.-Chim. Sin., 2002, 18, 332-335.
[23] W. Liao, T. Zheng, P. Wang, S. Tu, W. Pan, J. Environ. Sci. 2010, 22, 1800-1806.
[24] Y. L. Zi, L. Lin, J. Wang, S. H. Wang, J. Chen, X. Fan, P.-K. Yang, F. Yi, Z. L. Wang, Adv. Mater., 2015, 27, 2340-2347.
[25] R. A. Arndt, A. C. Damask, J. Chem. Phys., 1966, 45, 4627-4633.
[26] S. B. Lang, Br. Ceram. Trans., 2004, 103, 65-70.
[27] N. Guarrotxena, N. Vella, A. Toureille, J. L. Millán, Macromol. Chem. Phys., 1997, 198, 457-469.
[28] B. S. Kang, S. K. Choi, C. H. Park, J. Appl. Phys., 2003, 94, 1904-1911.
[29] J. F. Nye, Physical Properties of Crystals, Clarendon Press, Oxford, 1957.
[30] S. Bauer, S. B. Lang, IEEE Trans. Dielectr. Electr. Insul., 1996, 3, 647-676.
[31] Y. Yang, J. H. Jung, B. K. Yun, F. Zhang, K. C. Pradel, W. X. Guo, Z. L. Wang, Advanced Materials, 2012, 24, 5357-5362.
[32] M. A. Green, S. P. Bremner, Nat. Mater., 2016, 16, 23-34.
[33] C. Pavithra, W. Madhuri, J. Sol-Gel Sci. Technol., 2018, 85, 437-445.
[34] E. P. Smirnova, G. Yu. Sotnikova, N. V. Zaitseva, G. A. Gavrilov, A. V. Sotnikov, Phys. Solid State, 2019, 10, 1766-1771.
[35] Z. H. Dai, J. L. Xie, W. G. Liu, S. B. Ge, M. X. Fang, D. B. Lin, L. X. Pang, H. F. Ji, S. Zhou, X. B. Ren, Mater. Lett., 2019, 241, 55-59.
[36] D. Zekria, A. M. Glazer, V. Shuvaeva, J. Appl. Crystallogr., 2010, 37, 551-554.
[37] G. Xu, X. Huang, V. Krstic, S. Chen, X. Yang, C. Chao, G. Shen, G. Han, CrystEngComm, 2014, 16, 4373-4376.
[38] Y. F. Li, Z. P. Liu, J. Am. Chem. Soc., 2011, 133, 15743-15752.
[39] P. Dong, Y. Wang, H. Li, H. Li, X. Ma, L. Han, J. Mater. Chem. A, 2013, 1, 4651-4656.
[40] X. Meng, H. Qin, Z. Zhang, J. Colloid Interface Sci., 2018, 513, 877-890.
[41] M. Kurasawa, P. C. McLntyre, J. Appl. Phys., 2005, 97, 104110.

Pd/PbTiO₃表面的热电效应增强光催化Suzuki偶联反应

Pyroelectricity effect on photoactivating palladium nanoparticles in PbTiO₃ for Suzuki coupling reaction

PDF

Supporting Information

可视化

摘要/Abstract

引用本文

使用本文

扫码分享

参考文献

相关文章 15

编辑推荐

Metrics

[1]	赵彬彬, 钟威, 陈峰, 王苹, 别传彪, 余火根. 高晶化g-C₃N₄光催化剂: 合成、结构调控和光催化产氢[J]. 催化学报, 2023, 52(9): 127-143.
[2]	唐小龙, 李锋, 李方, 江燕斌, 余长林. 单原子催化剂在光催化和电催化合成过氧化氢中的研究进展[J]. 催化学报, 2023, 52(9): 79-98.
[3]	蔡铭洁, 刘艳萍, 董珂欣, 陈晓波, 李世杰. 漂浮型Bi₂WO₆/C₃N₄/碳布S型异质结光催化材料用于高效净化水体环境[J]. 催化学报, 2023, 52(9): 239-251.
[4]	王思恺, 闵祥婷, 乔波涛, 颜宁, 张涛. 单原子催化: 追寻催化领域的“圣杯”[J]. 催化学报, 2023, 52(9): 1-13.
[5]	江梓聪, 程蓓, 张留洋, 张振翼, 别传彪. 氧化锌基梯型异质结光催化剂[J]. 催化学报, 2023, 52(9): 32-49.
[6]	刘博文, 蔡家杰, 张建军, 谭海燕, 程蓓, 许景三. MOF/CdS梯型光催化剂同时进行苯甲醇氧化和析氢反应及其机理研究[J]. 催化学报, 2023, 51(8): 204-215.
[7]	宋明明, 宋相海, 刘鑫, 周伟强, 霍鹏伟. ZnIn₂S₄/MOF-808微球结构S型异质结光催化剂的制备及其光还原CO₂性能研究[J]. 催化学报, 2023, 51(8): 180-192.
[8]	邵秀丽, 李可, 李静萍, 程强, 王国宏, 王楷. 揭示NiS@Ta₂O₅纳米纤维中梯型电荷转移路径及光催化CO₂转化性能[J]. 催化学报, 2023, 51(8): 193-203.
[9]	李嘉明, 李源, 王小田, 杨直雄, 张高科. TiO₂上原子分散的Fe位点促进光催化CO₂还原: 增强的催化活性、 DFT计算和机制洞察[J]. 催化学报, 2023, 51(8): 145-156.
[10]	阎菲, 张由子, 刘思碧, 邹睿卿, Jahan B Ghasemi, 李炫华. 供体-受体型卟啉基金属有机框架实现有效电荷分离高效光催化析氢[J]. 催化学报, 2023, 51(8): 124-134.
[11]	孙利娟, 王伟康, 路平, 刘芹芹, 王乐乐, 唐华. 纳米高熵合金实现光催化剂肖特基势垒的调控用于光催化制氢与苯甲醇氧化耦合反应[J]. 催化学报, 2023, 51(8): 90-100.
[12]	刘海峰, 黄祥, 陈加藏. 电子态调控促进氢气无损耗纯化中CO的光致富集和氧化[J]. 催化学报, 2023, 51(8): 49-54.
[13]	袁鑫, 范海滨, 刘杰, 覃龙州, 王剑, 段秀, 邱江凯, 郭凯. 连续流技术在光氧化还原催化转化的最新进展[J]. 催化学报, 2023, 50(7): 175-194.
[14]	余治晗, 关晨, 岳晓阳, 向全军. 碳环渗入的结晶氮化碳S型同质结及其光催化析氢[J]. 催化学报, 2023, 50(7): 361-371.
[15]	李慧杰, 池漫洲, 辛兴, 王瑞杰, 刘天府, 吕红金, 杨国昱. 异金属取代的多金属氧酸盐@光响应型金属-有机框架用于高选择性光催化CO₂还原[J]. 催化学报, 2023, 50(7): 343-351.