CuO纳米片催化H2O2氧化降解亚甲基蓝

doi:10.1016/S1872-2067(12)60717-7

催化学报 ›› 2013, Vol. 34 ›› Issue (11): 2125-2129.DOI: 10.1016/S1872-2067(12)60717-7

CuO纳米片催化H₂O₂氧化降解亚甲基蓝

朱脉勇^a,b, 孟德海^a, 王程姣^a, 狄健^a, 刁国旺^a

a 扬州大学化学化工学院, 江苏扬州225002;
b 江苏大学材料科学与工程学院, 江苏镇江212013

收稿日期:2013-06-30 修回日期:2013-09-16 出版日期:2013-10-18 发布日期:2013-10-18
通讯作者: Guowang Diao
基金资助:
国家自然科学基金(20973151,21273195);扬州大学物理化学江苏省重大项目.

Degradation of methylene blue with H₂O₂ over a cupric oxide nanosheet catalyst

Maiyong Zhu^a,b, Dehai Meng^a, Chengjiao Wang^a, Jian Di^a, Guowang Diao^a

a College of Chemistry and Chemical Engineering, Yangzhou University, Yangzhou 225002, Jiangsu, China;
b School of Materials Science & Engineering, Jiangsu University, Zhenjiang 212013, Jiangsu, China

Received:2013-06-30 Revised:2013-09-16 Online:2013-10-18 Published:2013-10-18
Contact: Guowang Diao
Supported by:
This work was supported by the National Natural Science Foundation of China (20973151, 21273195) and the Foundation of Jiangsu Provincial Key Program of Physical Chemistry in Yangzhou University.

摘要/Abstract

摘要：

以十六烷基三甲基溴化铵(CTAB)为保护剂, 采用水热法成功制备了CuO纳米片. 将制备的CuO纳米片在H₂O₂存在下用于催化氧化降解亚甲基蓝, 探讨了其在不同反应条件(如温度、氧化剂浓度及催化剂用量)下对亚甲基蓝降解反应的影响. 该催化反应符合一级动力学模型, 活化能为54.0kJ/mol. CuO纳米片表现出非常高的催化活性, 但其稳定性与重复利用性有待于进一步提高.

关键词: 氧化铜, 纳米片, 亚甲基蓝, 氧化降解

Abstract:

Cupric oxide (CuO) nanosheets were prepared by the hydrothermal method with the use of cetyltrimethylammonium bromide (CTAB) and were used as the catalyst for the oxidation degradation of methylene blue with H₂O₂. The effects of temperature, oxidant concentration, and catalyst dosage were evaluated. The catalytic reaction obeyed first order kinetics, and the activation energy was 54 kJ/mol. Although the CuO nanosheets show high activity, their stability and reusability still need improvement.

Key words: Cupric oxide, Nanosheet, Methylene blue, Oxidation degradation

朱脉勇, 孟德海, 王程姣, 狄健, 刁国旺. CuO纳米片催化H₂O₂氧化降解亚甲基蓝[J]. 催化学报, 2013, 34(11): 2125-2129.

Maiyong Zhu, Dehai Meng, Chengjiao Wang, Jian Di, Guowang Diao. Degradation of methylene blue with H₂O₂ over a cupric oxide nanosheet catalyst[J]. Chinese Journal of Catalysis, 2013, 34(11): 2125-2129.

×
扫码分享

导出引用管理器 EndNote|Ris|BibTeX

链接本文: https://www.cjcatal.com/CN/10.1016/S1872-2067(12)60717-7

https://www.cjcatal.com/CN/Y2013/V34/I11/2125

参考文献

[1] Zollinger H. Color Chemistry: Synthesis, Properties and Applications of Organic Dyes and Pigments. VCH Publishers, New York, 1991. 379
[2] Morais L C, Freitas O M, Goncalves E P, Vasconcelos L T, Beca G C. Water Res, 1999, 33: 979
[3] Santhy K, Selvapathy P. Bioresour Technol, 2006, 97: 1329
[4] Zhu M Y, Diao G W. J Phys Chem C, 2011, 115: 18923
[5] Zhou L, Gao C, Xu W J. ACS Appl Mater Interfaces, 2010, 2: 1483
[6] Uddin M T, Islam M A, Mahmud S, Rukanuzzaman M. J Hazard Mater, 2009, 164: 53
[7] Francesca P, Sara M, Luigi T. Water Res, 2008, 42: 2953
[8] Zhang Z L, Chen H, Che H W, Wang Y H, Su F B. Mater Chem Phys, 2013, 138: 593
[9] Zhang Z L, Chen H, She X L, Sun J, Teo J, Su F B. J Power Sources, 2012, 217: 336
[10] Choi C S, Park Y U, Kim H, Kim N R, Kang K, Lee H M. Electrochim Acta, 2012, 70: 98
[11] Dubal D P, Gund G S, Holze R, Lokhande C D. J Power Sources, 2013, 242: 687
[12] Sukhorukov Y P, Gizhevskii B A, Mostovshchikova E V, Yermakov A Y, Tugushev S N, Kozlov E A. Tech Phys Lett, 2006, 32: 132
[13] Zhu M Y, Diao G W. Catal Sci Technol, 2012, 2: 82
[14] Zhang Z L, Che H W, Wang Y L, Gao J J, She X L, Sun J, Zhong Z Y, Su B. RSC Adv, 2012, 2: 2254
[15] Sun S D, Zhang X Z, Sun Y X, Yang S C, Song X P, Yang Z M. ACS Appl Mater Interfaces, 2013, 5: 4429
[16] Sun S D, Zhang X Z, Sun Y X, Yang S C, Song X P, Yang Z M. Phys Chem Chem Phys, 2013, 15: 10904
[17] Hong L, Liu A L, Li G W, Chen W, Lin X H. Biosens Bioelectron, 2013, 43: 1
[18] Zhu J, Qian X F. J Solid State Chem, 2010, 183: 1632
[19] Reddy K J, McDonald K J, King H. J Colloid Interface Sci, 2013, 397: 96
[20] Martinson C A, Reddy K J. J Colloid Interface Sci, 2009, 336: 406
[21] Meshram S P, Adhyapak P V, Mulik U P, Amalnerka, D P. Chem Eng J, 2012, 204-206: 158
[22] Hong J M, Li J, Ni Y H. J. Alloys Compounds, 2009, 481: 610

CuO纳米片催化H₂O₂氧化降解亚甲基蓝

Degradation of methylene blue with H₂O₂ over a cupric oxide nanosheet catalyst

PDF

可视化

摘要/Abstract

引用本文

使用本文

扫码分享

参考文献

相关文章 15

编辑推荐

Metrics

[1]	刘成, 陈梦宁, 时应章, 王志文, 郭韦, 林森, 毕进红, 吴棱. 超薄ZnTi-LDH纳米片作为一种具有路易斯酸和布朗斯特酸的双功能光催化剂用于串联反应合成N-亚苄基苯胺[J]. 催化学报, 2023, 49(6): 102-112.
[2]	朱可涵, 蒋海凤, 陈高锋, 吴昊, 丁良鑫, 王海辉. 耦合氨氧化和水还原反应实现电化学共合成硝酸盐和氢气[J]. 催化学报, 2023, 55(12): 216-226.
[3]	蒋婷婷, 谢伟伟, 耿仕鹏, 李如春, 宋树芹, 王毅. 构建氧空位调控的钼酸钴纳米片用于高效催化析氧反应[J]. 催化学报, 2022, 43(9): 2434-2442.
[4]	谢林峰, 刘轩, 黄凡洋, 梁嘉顺, 刘健云, 王谭源, 杨利明, 曹瑞国, 李箐. 通过金属间化合物PdBi纳米片调控Pd基催化剂电催化CO₂还原为甲酸盐[J]. 催化学报, 2022, 43(7): 1680-1686.
[5]	钱秀, 魏艳娇, 孙梦洁, 韩野, 张晓俐, 田健, 邵敏华. 在Ti₃C₂T_x MXene上原位生长2D TiO₂纳米片的异质结构用于改善电催化氮气还原[J]. 催化学报, 2022, 43(7): 1937-1944.
[6]	赵振龙, 边辑, 赵丽娜, 吴红君, 徐帅, 孙磊, 李志君, 张紫晴, 井立强. 2D ZnMOF/BiVO₄ S型异质结的构建及其可见光催化还原CO₂性能[J]. 催化学报, 2022, 43(5): 1331-1340.
[7]	熊伟, 周敏, 李昊, 丁朝, 张达, 吕耀康. 介孔氧化镍纳米片负载Pt纳米粒子电催化合成氨[J]. 催化学报, 2022, 43(5): 1371-1378.
[8]	程世群, 翁雪霏, 王庆楠, 周百川, 李文翠, 李名润, 贺雷, 王东琪, 陆安慧. 富缺陷BN负载的高分散Cu催化乙醇脱氢制乙醛[J]. 催化学报, 2022, 43(4): 1092-1100.
[9]	李婧宇, 祁明雨, 徐艺军. 超薄Ni掺杂ZnIn₂S₄纳米片用于光催化醇裂解同时制备C-C耦合产物及氢气[J]. 催化学报, 2022, 43(4): 1084-1091.
[10]	王琳琳, 李欣, 郝磊端, 洪崧, Alex W. Robertson, 孙振宇. 超细氧化铜纳米颗粒修饰二维金属有机框架协同增强二氧化碳电化学还原生成乙烯[J]. 催化学报, 2022, 43(4): 1049-1057.
[11]	孟祥东, 甄超, 刘岗, 成会明. Cu₃N保护壳层稳定CuO光阴极[J]. 催化学报, 2022, 43(3): 755-760.
[12]	白浚贤, 沈荣晨, 姜志民, 张鹏, 李佑稷, 李鑫. 集成二维层状CdS/WO₃ S型异质结及金属化Ti₃C₂ MXene基欧姆结高效光催化产氢[J]. 催化学报, 2022, 43(2): 359-369.
[13]	阮孙红, 张彪, 邹金含, 钟万福, 何潇洋, 卢进海, 张庆红, 王野, 谢顺吉. 高压下富含晶界的铋纳米片高效电还原CO₂制甲酸盐[J]. 催化学报, 2022, 43(12): 3161-3169.
[14]	武建栋, 赵晓, 崔小强, 郑伟涛. 新兴的二维金属烯: 结构调控和电催化应用进展[J]. 催化学报, 2022, 43(11): 2802-2814.
[15]	高学友, 曾德乾, 杨静仁, Ong Wee-Jun, Fujita Toyohisa, 何祥龙, 刘杰芡, 韦悦周. 超薄Ni(OH)₂纳米片修饰Zn_0.5Cd_0.5S纳米颗粒作为二维/零维异质结构光催化剂可见光下光催化制氢[J]. 催化学报, 2021, 42(7): 1137-1146.